MULTIFUNCTIONAL COATINGS AND ADHESIVE COMPOSITIONS FOR FASTENERS
A coating composition comprises: A) an epoxy curing agent component; B) a microencapsulated epoxy resin component; C) an expansion agent component; D) a binder component; and E) a solvent component. In various embodiments, components B) and C) are present in a weight ratio of from about 20:1 to about 1:20. An ultraviolet-curable coating composition comprises components A), B), C) and D). The ultraviolet-curable coating composition further comprises F) a photoinitiator component. After rupture of component B), the compositions cure to form an adhesive. The compositions are useful for fasteners (e.g. screws and bolts) such that they can be referred to as fastener adhesives. A powdered adhesive composition comprises components A), B) and C). The powdered adhesive composition is substantially anhydrous and/or substantially free of a solvent (e.g. component E)). The powdered adhesive composition is useful for securing a fastener (e.g. in a borehole).
1 . A coating composition for forming a fastener adhesive, said coating composition comprising:
A) an epoxy curing agent component;
B) a microencapsulated epoxy resin component;
C) an expansion agent component;
D) a binder component; and
E) a solvent component;
wherein the microencapsulated epoxy resin component B) and the expansion agent component C) are present in a weight ratio of from about 20:1 to about 1:20.
2 . The coating composition according to claim 1 , wherein the microencapsulated epoxy resin component B) and the expansion agent component C) are present in a weight ratio of from about 15:1 to about 1:1, or optionally in a weight ratio of from about 4:1 to about 2:1.
3 . The coating composition according to claim 1 , wherein the epoxy curing agent component A): i) comprises an amine; ii) is present in an amount of from about 1 to about 20 part(s) by weight based on 100 parts by weight of the composition; or iii) both i) and ii).
4 . The coating composition according to claim 1 , wherein the microencapsulated epoxy resin component B): i) comprises a novolac epoxy resin, a bisphenol F epoxy resin, or a combination thereof; ii) is present in an amount of from about 20 to about 50 parts by weight based on 100 parts by weight of the composition; or iii) both i) and ii).
5 . The coating composition according to claim 1 , wherein the expansion agent component C): i) comprises a microencapsulated expansion agent; ii) is present in an amount of from about 1 to about 25 part(s) by weight based on 100 parts by weight of the composition; or iii) both i) and ii).
6 . The coating composition according to claim 1 , wherein the binder component D): i) comprises an acrylic resin; ii) is present in an amount of from about 1 to about 10 part(s) by weight based on 100 parts by weight of the composition; or iii) both i) and ii).
7 . The coating composition according to claim 1 , wherein the solvent component E): i) comprises an organic solvent; ii) is present in an amount of from about 20 to about 50 parts by weight based on 100 parts by weight of the composition; or iii) both i) and ii).
8 . The coating composition according to claim 1 , further comprising an anti-settling component, a colorant component, or a combination thereof.
9 . (canceled)
10 . An adhesive formed by curing the composition as set forth in claim 1 .
11 . An article comprising:
a substrate having a surface; and
an adhesive composition disposed on the surface;
wherein the adhesive composition is prepared from the coating composition as set forth in claim 1 .
12 . A fastener comprising the article as set forth in claim 11 , wherein the substrate surface comprises a threaded surface.
13 . The fastener as set forth in claim 12 , wherein the substrate is selected from the group consisting of anchors, bolts, nuts, screws, studs, stand-offs, plugs/caps, and combinations thereof.
14 . An assembly including a fastener, wherein the fastener is as set forth in claim 13 and wherein the adhesive composition expands and cures to form an adhesive.
15 . A method of making an article, said method comprising the steps of:
providing a substrate having a surface;
providing an adhesive composition; and
applying the adhesive composition to the surface of the substrate;
wherein the adhesive composition is the coating composition as set forth in claim 1 .
16 . The method according to claim 15 , further comprising the step of drying the adhesive composition after application.
17 . The method according to claim 15 or 16 , further comprising the step of applying an overcoat composition to the applied adhesive composition to form a sacrificial layer thereon.
18 - 23 . (canceled)
24 . A method for joining a fastener and an element defining a borehole, said method comprising the steps of:
providing the fastener;
providing a composition;
disposing the composition into the borehole; and
disposing the fastener into the borehole;
wherein the composition is the coating composition as set forth in claim 1 ;
wherein the composition is disposed at least partially between the fastener and the borehole to form a joint; and
wherein the composition expands and cures in the joint to fasten the fastener in the borehole.
25 . (canceled)
26 . (canceled)
27 . The method according to claim 24 , further comprising the step(s) of applying the coating composition to a permeable carrier, and optionally drying the coating composition, prior to the step of disposing the composition into the borehole.
28 . The method according to claim 24 , further comprising the step(s) of forming the borehole in the element, and optionally cleaning at least a portion of the borehole, prior to the step of disposing the composition into the borehole.
29 . The method according to claim 24 , wherein: i) the fastener is an anchor or screw; ii) the element comprises at least one of cement, concrete, or mortar; or iii) both i) and ii).
30 . (canceled)