Molded articles, and methods thereof

1. A molded article formed from a blend, the blend comprising:

from 1 wt. % to 30 wt. % of a polypropylene homopolymer; and

from 60 wt. % to 99 wt. % of an ionomer formed from a partially neutralized precursor acid copolymer, wherein the precursor acid copolymer (a) comprises copolymerized units of ethylene and 5 wt. % to 30 wt. %, based on the total weight of the precursor acid copolymer, of copolymerized units of an α,β-ethylenically unsaturated carboxylic acid having 3 to 8 carbon atoms, and (b) has a melt index, I2, (according to ASTM D1238 at 190° C., 2.16 kg) of 100 g/10 min to 450 g/10 min, and wherein about 25% to about 65% of the acid groups derived from the α,β-ethylenically unsaturated carboxylic acid of the precursor acid copolymer are neutralized; and

wherein the acid groups derived from the α,β-ethylenically unsaturated carboxylic acid of the precursor acid copolymer are neutralized by a sodium-ion-containing base; and

wherein the ionomer has a melt index, I2, (according to ASTM D1238 at 190° C., 2.16 kg) of 3 g/10 min to 15 g/10 min; and

wherein the molded article has an internal haze from 2.1% to 6.1%.

2. The molded article of claim 1 , wherein the ionomer has a freeze enthalpy that is not detectable or is less than about 3.0 J/g.

3. The molded article of claim 1 , wherein the molded article is an injection molded article.

4. The molded article of claim 1 , wherein the molded article is a compression molded article.

5. A method of manufacturing a molded article, the method comprising:

providing a blend comprising from 1 wt. % to 30 wt. % of a polypropylene homopolymer; and from 60 wt. % to 99 wt. % of an ionomer formed from a partially neutralized precursor acid copolymer, wherein the precursor acid copolymer (a) comprises copolymerized units of ethylene and 5 wt. % to 30 wt. %, based on the total weight of the precursor acid copolymer, of copolymerized units of an α,β-ethylenically unsaturated carboxylic acid having 3 to 8 carbon atoms, and (b) has a melt index, I2, (according to ASTM D1238 at 190° C., 2.16 kg) of 100 g/10 min to 450 g/10 min, and wherein about 25% to about 65% of the acid groups derived from the α,β-ethylenically unsaturated carboxylic acid of the precursor acid copolymer are neutralized; and

molding the blend into a molded article; and

wherein the acid groups derived from the α,β-ethylenically unsaturated carboxylic acid of the precursor acid copolymer are neutralized by a sodium-ion-containing base; and

wherein the ionomer has a melt index, I2, (according to ASTM D1238 at 190° C., 2.16 kg) of 3 g/10 min to 15 g/10 min; and

wherein the molded article has an internal haze from 2.1 to 6.1%.

6. The method of claim 5 , wherein molding is done by injection molding.

7. The method of claim 5 , wherein molding is done by compression molding.

8. The method of claim 5 , wherein the ionomer has a freeze enthalpy that is not detectable or is less than about 3.0 J/g.

9. The molded article of claim 1 , wherein the molded article has an oven creep (85° C., 30 g) form 50% to 131% elongation after 160 minutes.

10. The molded article of claim 1 , wherein the polypropylene homopolymer has a melt flow rate (according to ASTM D1238 at 230° C., 2.16 kg) of 5 g/10 min to 20 g/10 min.

11. The molded article of claim 1 , wherein the polypropylene homopolymer has a density from 0.895 g/cc to 0.908 g/cc.

12. The method of claim 5 , wherein the molded article has an oven creep (85° C., g) form 50% to 131% elongation after 160 minutes.

13. The method of claim 5 , wherein the polypropylene homopolymer has a melt flow rate (according to ASTM D1238 at 230° C., 2.16 kg) of 5 g/10 min to 20 g/10 min.

14. The method of claim 5 , wherein the polypropylene homopolymer has a density from 0.895 g/cc to 0.908 g/cc.