Silicon-oxygen compound, secondary battery using it, and related battery module, battery pack and device
The present application provide a silicon-oxygen compound, a secondary battery using it, and related battery modules, battery packs, and devices. The silicon-oxygen compound provided by the present application has a formula of SiO x , in which x satisfies 0<x<2. The silicon-oxygen compound contains both sulfur and aluminum element, and the sulfur element is present in an amount of 20 ppm˜300 ppm. The mass ratio of sulfur element to aluminum element is from 1.5 to 13.0. A secondary battery uses the silicon-oxygen compound provided in the present application, so that the secondary battery can have both long-cycle performance and high initial coulombic efficiency.
1. A silicon-oxygen compound having a formula of SiO x , in which 0<x<2, characterized in that, the silicon-oxygen compound contains both sulfur and aluminum element, and a content of the sulfur element is 20 ppm˜300 ppm; and a mass ratio of the sulfur element to the aluminum element is from 1.5 to 13.0;
in X-ray diffraction pattern of the silicon-oxygen compound, there is a diffraction peak at a position where the diffraction angle 2θ is 26°-30°, and the full width at half maxima of the diffraction peak is 0.8°-3.2°;
there is a diffraction peak at a position where the diffraction angle 2θ is 46°-50°, and the full width at half maxima of the diffraction peak is 1.0°-4.2°;
there is a diffraction peak at a position where the diffraction angle 2θ is 54°-58°, and the full width at half maxima of the diffraction peak is 0.8°-4.5°.
2. The silicon-oxygen compound according to claim 1 , characterized in that, the content of the sulfur element is from 30 ppm to 250 ppm.
3. The silicon-oxygen compound according to claim 1 , characterized in that, the content of the aluminum element is from 5 ppm to 150 ppm.
4. The silicon-oxygen compound according to claim 1 , characterized in that, the mass ratio of the sulfur element to the aluminum element is from 2.0 to 10.0.
5. The silicon-oxygen compound according to claim 1 , characterized in that, the silicon-oxygen compound has a powder volume resistivity under a pressure of 20 MPa of 10 Ω·cm or less.
6. The silicon-oxygen compound according to claim 1 , characterized in that, the silicon-oxygen compound has an average particle diameter Dv50 of 2 μm˜15 μm.
7. The silicon-oxygen compound according to claim 1 , characterized in that, the silicon-oxygen compound has a specific surface area from 1 m 2 /g to 7 m 2 /g.
8. The silicon-oxygen compound according to claim 1 , characterized in that, the silicon-oxygen compound has a compacted density measured under a pressure of 5 tons (equivalent to 49 KN) of 1.2 g/cm 3 ˜1.7 g/cm 3 .
9. The silicon-oxygen compound according to claim 1 , characterized in that, a coating layer is coated on an outer surface of the silicon-oxygen compound, and the coating layer comprises one or more of a polymer, a carbon material, and a metal compound.
10. A secondary battery, characterized in that, the secondary battery comprises the silicon-oxygen compound according to claim 1 .
11. A device, characterized in that, the device comprises at least one of the secondary battery of claim 10 .
12. The silicon-oxygen compound according to claim 1 , wherein the content of the aluminum element is from 10 ppm to 100 ppm.
13. The silicon-oxygen compound according to claim 1 , wherein the silicon-oxygen compound has a powder volume resistivity under a pressure of 20 MPa of 1 Ω·cm or less.
14. The silicon-oxygen compound according to claim 1 , wherein the silicon-oxygen compound has an average particle diameter Dv50 of 3 μm˜12 μm.
15. The silicon-oxygen compound according to claim 1 , wherein the silicon-oxygen compound has a specific surface area from 2 m 2 /g to 6 m 2 /g.
16. The silicon-oxygen compound according to claim 1 , wherein the silicon-oxygen compound has a compacted density measured under a pressure of 5 tons (equivalent to 49 KN) of 1.3 g/cm 3 ˜1.6 g/cm 3 .