Method for producing acrylic solid surface with improved color and scratch appearance
This technology is directed to a well-dispersed micronized pigment (carbon black and/or metal oxides such as iron oxide and zinc sulfide) which is added to Aristech's acrylic solid surface formulation at 0.5-5 wt % resulting in a solid surface with an enriched color and improved surface scratch appearance. The use of the micronized pigments helps surface scratches appear less white because of the improved coverage of white aluminum trihydrate (ATH).
1. An acrylic composition, comprising:
about 20-35% acrylic pre-polymerized syrup by weight;
about 5-20% methyl methacrylate by weight;
about 5-70% of aluminum trihydrate particulate by weight;
about 0.5-5% of a micronized pigment by weight, wherein the micronized pigment is selected from the group consisting of carbon black, iron oxide, zinc sulfide, and any combination thereof; and
a liquid dispersion comprising the micronized pigment and a liquid carrier, wherein the liquid carrier is selected from the group consisting of benzoate ester, butyl acrylate, n-butyl methacrylate, and any combination thereof, wherein the micronized pigment is dispersed in the liquid carrier.
2. The acrylic composition of claim 1 , wherein the micronized pigment is about 0.5-1 wt %.
3. The acrylic composition of claim 1 , wherein the alumina trihydrate particulate is treated with 3-methacryloxypropyl trimethoxy silane.
4. The acrylic composition of claim 1 , wherein the acrylic pre-polymerized syrup is at 20% solids.
5. The acrylic composition of claim 1 , wherein the micronized pigment comprises carbon black.
6. A method comprising:
preparing the acrylic composition of claim 1 ;
mixing the acrylic composition such that the micronized pigment bonds to the surface of the aluminum trihydrate particulate;
combining the mixed acrylic composition with one or more initiators to form a liquid mixture; and
casting the liquid mixture to form a sheet.
7. The method of claim 6 , wherein casting the liquid mixture comprises transferring the liquid mixture to a continuous casting machine.
8. The method of claim 6 , wherein preparing the acrylic composition comprises combining the acrylic pre-polymerized syrup, methyl methacrylate, and aluminum trihydrate particulate to form a dispersion; and filtering the dispersion by a 250 to 400 micron filter.
9. The method of claim 6 , wherein the aluminum trihydrate particulate is treated with a coupling agent prior to preparing the acrylic composition.
10. The method of claim 6 , wherein the micronized pigment is carbon black.
11. The method of claim 6 , wherein the micronized pigment is present in an amount of about 0.5-1% by weight of the acrylic composition.