One-pot process of making silicone-acrylic hybrid pressure sensitive adhesive compositions

1. A one-pot process of making a single-phase silicone-acrylic hybrid composition comprising the steps of:

(a) making an acrylic polymer solution by a free radical polymerization in an organic solution;

(b) adding (i) a silicone polymer and (ii) a catalyst to the acrylic polymer solution and reacting to form a silicone-acrylic hybrid solution;

(c) neutralizing the silicone-acrylic hybrid solution with a neutralization reagent,

(d) filtering any solid precipitates from the silicone-acrylic hybrid solution to form a single-phase silicone acrylic hybrid composition in solution;

wherein the ratio of the silicone polymer and the acrylic polymer is from 50:1 to 1:50,

wherein the silicon-acrylic hybrid composition comprises —Si—O—Si— covalent bond linkages between the silicone polymer and the acrylic polymer;

wherein the one-pot process is conducted in a single reaction setting; and

wherein the silicon-acrylic hybrid composition remains as a single-phase for over six months.

2. A one-pot process of making a single-phase silicone-acrylic hybrid composition comprising the steps of:

(a) making an acrylic polymer solution by polymerizing:

(i) a mixture of monomers, wherein at least one monomer comprises a hydrolyzable silane (meth)acrylic monomer and/or a siloxane (meth)acrylic macromer,

(ii) a free radical initiator,

(iii) an organic solvent,

wherein the reaction temperature is from about 50 to about 150° C., and reaction time is from about 2 to 24 hr;

(b) adding (i) a silicone polymer, and (ii) a catalyst into the acrylic polymer solution (a) and reacting at a reaction temperature of about 50 to about 150° C. for about 2 to 24 hours to form a silicone-acrylic hybrid solution;

(c) neutralizing the silicone-acrylic hybrid solution at a temperature of about room temperature to about 150° C. for about 2 to 24 hours; and

(d) filtering any solid precipitates from the silicone-acrylic hybrid solution to form a single-phase silicone acrylic hybrid composition in solution;

wherein the ratio of the silicone polymer and the acrylic polymer is from 50:1 to 1:50,

wherein the silicon-acrylic hybrid composition comprises —Si—O—Si— covalent bond linkages between the silicone polymer and the acrylic polymer;

wherein the one-pot process is conducted in a single reaction setting; and

wherein the silicon-acrylic hybrid composition remains as a single-phase for over six months.

3. The one-pot process of claim 1 , wherein the step (a) making of acrylic polymer is formed in the presence of the silicone polymer (b)(i).

4. The one-pot process of claim 2 wherein the hydrolyzable silane (meth)acrylic monomer and/or the siloxane (meth)acrylic macromer is in the content of about 0.1 to about 50 wt % based on the total weight of acrylic monomers.

5. The one-pot process of claim 2 , wherein the hydrolyzable silane (meth)acrylic monomer (a)(i) has a formula of

CH 2 ═CHR′COO—X—SiR” n-3 Y n , wherein

R′ is H or methyl group; R” is selected from the group consisting of alkyl, aryl, fluoroalkyl, trialkylsilyl, triarylsilyl, vinyl, or combination thereof;

X is a linear, cyclic, or branched divalent link selected from the group of alkylene, arylene, oxyalkylene, oxyarylene, ester, amine, glycol, imide, amide, alcohol, carbonate, urethane, urea, sulfide, ether, or a derivative or combination thereof; and

Y is selected from the hydrolyzable group consisting of alkoxy, aryloxy, acetoxy, oximino, enoxy, amino, amido, α-hydroxycarboxylic acid amide (—OCR′ 2 CONR”2), α-hydroxycarboxylic acid ester (—OCR′2COOR”), H, halogen, or combination thereof; n is selected from 1, 2, and 3.

6. The one-pot process of claim 4 , wherein the siloxane (meth)acrylic macromer (a)(i) is a mono(meth)acrylate terminated polydimethylsiloxane polymer or oligomer.

7. The one-pot process of claim 2 , wherein the monomers (a)(i) further comprises a second monomer that has a formula of

CH 2 ═CR 1 R 2 , wherein

R 1 is H or methyl group;

R 2 is selected from the group consisting of COOR 3 , OCOR 3 , aryl, heterocyclic, or combination thereof;

R 3 is selected from the group consisting of H, alkyl, aryl, allyl, fluoroalkyl, hydroxyalkyl, trialkylsilyl, triarylsilyl, epoxyalkyl, aminoalkyl, ammoniumalkyl or combination thereof.

8. The one-pot process of claim 7 , wherein the second monomer is selected from the group consisting of methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, isooctyl (meth)acrylate, t-octyl (meth)acrylamide, hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, 2-(ciimethylamino)ethyl (meth)acrylate, [2-(acryloyloxy)ethyl]trimethylammonium, (meth)acrylic acid, 2-carboxyethyl acrylate, vinyl acetate, 1-vinyl-2-pyrrolidinone, styrene, α-methylstyrene, or combination thereof.

9. The one-pot process of claim 2 , wherein the radical initiator (a)(ii) is selected from the group consisting of 2,2′-azobisisobutyronitrile, 1,1′-azobis(cyclohexanecarbonitrile), 2,2′-azodi(2-methylbutyronitrile), 4,4-azobis(4-cyanovaleric acid), 1,1′-azobis(cyanocyclohexane), 2-2′-Azobis(2,4-dimethylvaleronitrile), 2,2-bis(tert-butylperoxy)butane, test-amyl peroxypivalate, cyclohexanone peroxide, benzoyl peroxide, or combination thereof.

10. The one-pot process of claim 2 , wherein the organic solvent (a)(iii) is selected from the group consisting of aliphatic hydrocarbons, aromatic hydrocarbon, ether, ketone, alcohol, alkyl acetate, tetrahydrofuran, water and mixtures thereof.

11. The one-pot process of claim 1 , wherein the (b)(i) silicone polymer is a siloxane polymer, a silicone resin, or combination of the two with a ratio range from about 9:1 to 1:9.

12. The one-pot process of claim 11 , wherein the siloxane polymer is a diorganosubstituted polysiloxane that has terminal group selected from hydrolyzable hydroxyl, alkoxy hydride, or combination thereof.

13. The one-pot process of claim 11 , wherein the siloxane polymer has weight average molecular weight of from about 100 g/mol to 3,000,000 g/mol.

14. The one-pot process of claim 11 , wherein the silicone resin comprises at least one tetrafunctional siloxyl unit SiO 4/2 and at least one triorganosiloxy unit R 3 SiO 1/2 , wherein the R is methyl, hydroxyl, vinyl, phenyl, (meth)acryloxy, or combination thereof, and the mole ratio of the units SiO 4/2 to R 3 SiO 1/2 is from 1:2 to 2:1; wherein the R is from about 0.05 wt % to 10 wt % based on the total weight of the silicone resin.

15. The one-pot process of claim 14 , wherein the silicone resin has weight average molecular weight of from about 100 g/mol to 3,000,000 g/mol.

16. The one-pot process of claim 2 , wherein the (b)(ii) catalyst has a pKa value of ≤6 or ≥15.

17. The one-pot process of claim 16 , wherein catalyst is selected from MOR, wherein M is Cs, Rb, K, Na, Li and R is H, alkyl, aryl, allyl, fluoroalkyl, or combination thereof; organolithium reagents, Grignard reagents, methanesulfonic acid, sulfuric acid, acidic clay, Lewis acid, acidic ion exchange resins, or combination thereof.

18. The one-pot process of claim 1 , wherein the neutralization reagent is selected from dilute hydrochloric acid (aq), chlorotrimethylsilane, fume silica, sodium carbonate, sodium bicarbonate, calcium carbonate, acetic acid, ammonium hydroxide(aq), ammonium carbonate, hexamethyldisilazane, aminopropyltrimethylsilane, propylene epoxide, carbon dioxide gas or combination thereof.

19. The one-pot process of claim 1 , further comprising step (e) adding an additive to the silicone-acrylic hybrid pressure sensitive adhesive composition, wherein the additive is selected from the group consisting of tackifiers, additional polymers, silicon oils, plasticizers, diluents, solubilizing agents, organic or inorganic fillers, pigments, fluorescent additives, flow and leveling additives, wetting agents, surfactants, antifoaming agents, rheology modifiers, emulsifiers, humectants, gelling agent, colorants, other surface modifying agents, fragrances, permeation enhancers, stabilizers, antioxidants, and combination thereof.

20. A process for making a transdermal device comprising a silicone-acrylic hybrid pressure sensitive adhesive (PSA) composition and an active in a one-pot process comprising the steps of.

(a) making an acrylic polymer by a polymerization reaction of (i) a mixture of monomers, wherein at least one monomer comprises a hydrolyzable silane (meth)acrylic monomer and/or a siloxane (meth)acrylic macromer, (ii) a radical initiator; (iii) an organic solvent, and

(b) adding (i) a silicone polymer and (ii) a base or an acid catalyst into the acrylic polymer solution (a) and reacting at a temperature of about 50 to about 150° C. for about 2 to about 24 hours to form a silicone-acrylic hybrid solution;

(c) neutralizing the solution (b) at a temperature of about room temperature to about 150° C. for about 2 to 24 hours;

(d) removing any solid precipitates to form a single-phase silicone-acrylic hybrid PSA composition;

(e) adding the active to the solution (d), wherein the active is a pharmaceutical, nutraceutical and/or cosmeceutical agent;

(f) applying the solution (e) onto a film substrate; and

(g) evaporating the solvent to form a transdermal device

wherein the one-pot process is conducted in a single reaction setting; and

wherein the silicon-acrylic hybrid pressure sensitive adhesive composition remains as a single-phase for over six months.