Thermoplastic elastomeric formulation
A thermoplastic elastomeric formulation comprises (i) a water based thermoplastic elastomer (TPE), (ii) a surfactant, (iii) an antioxidant, (iv) a antifoaming agent and (v) a crosslinking agent. The water based TPE is styrene-isoprene-styrene (SIS) copolymer latex. A glove that is produced using the thermoplastic elastomeric formulation of the present invention is known as water based TPE gloves, such as water based TPE medical exam gloves, water based TPE household gloves and water based TPE industrial gloves in particular water based TPE surgical gloves.
1. A thermoplastic elastomeric formulation that is free of an accelerator comprising:
(i) a water based thermoplastic elastomer (TPE) in an amount of 100 phr,
wherein the water based TPE is styrene-isoprene-styrene (SIS) copolymer latex;
(ii) a surfactant in a range of 0.30 phr to 0.50 phr,
wherein the surfactant is any one selected from a group consisting of an amphoteric surfactant and an anionic surfactant;
(iii) an antioxidant in a range of 1 .00 phr to 3.00 phr,
wherein the antioxidant is any one selected from a group consisting of thiophenolic type antioxidant which is 2,6-di-tert-butyl-4-(4.6-bis(octylthio)-1.3,5-triazin-2-ylamino)phenol, poly(dicyclopentadiene-co-p-cresol) and alkylated diphenylamines;
(iv) an antifoaming agent in a range of 0.02 phr to 0.06 phr,
wherein the antifoaming agent is any one selected from a group consisting of polvdimethylsiloxane, emulsion of modified silicone, mixture of polypropylene based and polyether dispersion, and
(v) a crosslinking agent in a range of 0.50 phr to 2.00 phr,
wherein the crosslinking agent is any one selected from a group consisting of bivalent and trivalent ionic compound including aluminium hydroxide and zinc oxide.
2. The thermoplastic elastomeric formulation as claimed in claim 1 , wherein the (SIS)copolymer latex having styrene in a ratio of 15% to 35% and isoprene in a ratio of 65% to 85%.
3. A glove having the thermoplastic elastomeric formulation as claimed in claim 2 .
4. The glove as claimed in claim 3 , wherein the glove is a water based TPE surgical glove.
5. The thermoplastic elasto eric formulation as claimed in claim 1 , wherein the amphoteric surfactant is monosodium N-Lauryl-beta-Iminodipropionic acid.
6. A glove having the thermoplastic elasterneric formulation as claimed in claim 5 .
7. The glove as claimed in claim 6 , wherein the glove is a water based TPE surgical glove.
8. The thermoplastic elastomeric formulation as claimed in claim 1 , wherein the anionic surfactant is any one selected from the group consisting of sodium dodecylbenzene sulphonate, alkyldiphenyloxide disulphonate, dioctyl sulphosuccinates and alkyl benzene sulphonate.
9. A glove having the thermoplastic elastomeric formulation as claimed in claim 1 .
10. The glove as claimed in claim 9 , wherein the glove is a water based TPE surgical glove.
11. A glove having the thermoplastic elastomeric formulation as claimed in claim 8 .
12. The glove as claimed in claim 11 , wherein the glove is a water based TPE surgical glove.