Polyester film and flexible display apparatus comprising same
The polyester film according to an embodiment has a coefficient of determination (R 2 ) of the strain with respect to stress and a crystallinity adjusted to specific ranges, whereby it is possible to achieve the flexibility that does not cause deformation even when a certain stress is sustained for a long period of time and the resistant characteristics to the impact of external pressing. Accordingly, the polyester film can be applied to a cover of a flexible display device, in particular, a foldable display device to exhibit excellent characteristics.
1. A polyester film having a coefficient of determination (R 2 ) of 0.985 or more in first and second directions perpendicular to each other in a plane, respectively, in the section in which the strain is 2% to 3% in the stress-strain curve and having a crystallinity of 55% or more,
wherein the polyester film has a difference between the stress at a strain of 2% and the stress at a strain of 4% in the stress-strain curve of 10 MPa or more.
2. The polyester film of claim 1 , which has a coefficient of determination (R 2 ) of 0.990 or more in the section in which the strain is 0% to 2% in the stress-strain curve.
3. The polyester film of claim 1 , which has a stress at a strain of 4% in the stress-strain curve of 65 MPa to 85 MPa.
4. The polyester film of claim 1 , which has a strain for a stress of 80 MPa in the stress-strain curve of 3% to 8%.
5. The polyester film of claim 1 , which is biaxially stretched, wherein the ratio between the respective stretching ratios in the two directions is 1:0.8 to 1:1.2.
6. The polyester film of claim 1 , which is subjected to thermal treatment at a temperature of 195° C. or higher.
7. The polyester film of claim 1 , which withstands 200,000 times or more of repeated folding until it is deformed.
8. The polyester film of claim 1 , which is applied to a cover of a flexible display device.
9. A laminate, which comprises a transparent cover for a flexible display device; and a polyester film disposed on the transparent cover,
wherein the polyester film has a coefficient of determination (R 2 ) of 0.985 or more in first and second directions perpendicular to each other in a plane, respectively, in the section in which the strain is 2% to 3% in the stress-strain curve and has a crystallinity of 55% or more,
wherein the polyester film has a difference between the stress at a strain of 2% and the stress at a strain of 4% in the stress-strain curve of 10 MPa or more.
10. The laminate of claim 9 , wherein the transparent cover is a polyimide-based film or ultra-thin glass (UTG), and the laminate withstands 200,000 times or more of repeated folding until it is delaminated.
11. A flexible display device, which comprises a flexible display panel; and a polyester film disposed on the flexible display panel,
wherein the polyester film has a coefficient of determination (R 2 ) of 0.985 or more in first and second directions perpendicular to each other in a plane, respectively, in the section in which the strain is 2% to 3% in the stress-strain curve and has a crystallinity of 55% or more
wherein the polyester film has a difference between the stress at a strain of 2% and the stress at a strain of 4% in the stress-strain curve of 10 MPa or more.