Malleable demineralized bone composition and method of manufacture
A malleable demineralized bone composition consists of cortical bone made from a first portion and a second portion. The first portion and second portion of cortical bone is made from cut pieces freeze dried then ground into particles and demineralized then freeze-dried. A volume of the second portion is placed in a solution of sterile water to create a mixture, the water volume being seven times the volume of the second portion, the mixture is autoclaved under heat and pressure to form a gelatin, and the first portion is mixed with the gelatin to form a malleable putty or paste.
1. A method of making a malleable demineralized bone composition consisting of cortical bone, comprising the steps of
a) preparing cortical bone by cutting the cortical bone into pieces, freeze-drying the pieces and then grinding into particles and demineralizing the ground particles and freeze-drying the demineralized ground particles to form freeze-dried demineralized bone matrix (DBM) particles;
b) dividing the freeze-dried DBM particles into a first portion and a second portion;
c) autoclaving a volume of the second portion of DBM particles mixed with sterile water to form a gelatin;
d) cooling the gelatin; and
e) mixing the freeze-dried ground particles of the first portion with the gelatin from the second portion at a ratio of 80:20 or less gelatin to DBM to create a malleable and cohesive putty or paste, wherein the malleable and cohesive putty or paste is moldable into different shapes with no visible cracks and maintains its shape while immersed in normal saline or water for a minimum of one minute.
2. A method of making a malleable demineralized bone composition consisting of cortical bone comprising:
a) preparing a first portion of cortical bone by cutting the cortical bone into pieces, freeze-drying the pieces and then grinding into particles and demineralizing the ground particles and thereafter freeze-drying the demineralized ground particles to form a first portion of demineralized bone matrix (DBM) particles;
b) preparing a second portion of cortical bone by shaving cortical bone plates cut into 6.5 cm long pieces, wherein cortical bone is cut into long pieces from the cortical bone plates, cleaned and then shaved to form shavings of cortical bone tissue then freeze-drying the shavings, grinding the freeze-dried shavings to obtain a particle size less than 150 μm, and demineralizing the particles thereafter freeze-drying to form a second portion of DBM particles;
c) autoclaving a volume of the second portion of DBM particles mixed with sterile water to form a gelatin;
d) cooling the gelatin made from the second portion; and
e) mixing the freeze-dried ground particles of the first portion with the gelatin from the second portion at a ratio of 80:20 or less gelatin to DBM to create a malleable and cohesive putty or paste, wherein the malleable and cohesive putty or paste is moldable into different shapes with no visible cracks and maintains its shape while immersed in normal saline or water for a minimum of one minute.