Recycled and renewable polymeric composition for computer chassis
Polymeric compositions, methods of making the compositions, and composites, such as computer chassis containing the compositions are described. The polymeric compositions can contain 20 wt. % to 50 wt. % of a post-consumer mechanical recycled polycarbonate; 10 wt. % to 50 wt. % of a renewably sourced polycarbonate; 10 wt. % to 30 wt. % of a filler containing carbon fibers, wherein at least a portion of the carbon fibers are obtained from a post-industrial recycled source; and 5 wt. % to 15 wt. % of a flame retardant, wherein the polymeric compositions have a total recycled and renewable content of 50 wt. % to 90 wt. %.
1. A polymeric composition comprising:
20 wt. % to 50 wt. % of post-consumer mechanical recycled polycarbonate;
10 wt. % to 50 wt. % of renewably sourced polycarbonate, at least a portion of the renewably sourced polycarbonate being renewable content;
10 wt. % to 30 wt. % of a filler comprising carbon fibers, wherein at least a portion of the carbon fibers are obtained from a post-industrial recycled source; and
5 wt. % to 15 wt. % of a flame retardant,
wherein the polymeric composition comprises a total recycled and renewable content of 50 wt. % to 90 wt. %.
2. The polymeric composition of claim 1 , wherein the renewably sourced polycarbonate is produced, at least in part, from a renewable feedstock such that the renewable content is 13 wt. % to 65 wt. % of the renewably sourced polycarbonate.
3. The polymeric composition of claim 2 , wherein the renewable feed stock comprises one or more of tall oil, caster beans, sugar, and waste carbon dioxide (CO 2 ).
4. The polymeric composition of claim 1 , wherein 10 wt. % to 30 wt. % of the carbon fibers are obtained from post-industrial recycled source.
5. The polymeric composition of claim 1 , wherein the carbon fibers are standard modulus fibers, intermediate modulus fibers, and/or high strength carbon fibers.
6. The polymeric composition of claim 1 , wherein the flame retardant is obtained from a renewable source.
7. The polymeric composition of claim 6 , wherein the flame retardant is a non-halogenated phosphorus containing flame retardant obtained from bio based chemicals.
8. The polymeric composition of claim 1 , further comprising an additive, wherein the additive is a pigment, a plasticizer, an antioxidant, an UV-stabilizer, a heat stabilizer, a dye enhancing agent, a lubricant, a mold release agent, a crystal nucleating agent, a fluidability-improving agent, an antistatic agent, a compatibilizer, or an anti-drip agent, or any combination thereof.
9. The polymeric composition of claim 8 , comprising 0.1 wt. % to 3 wt. % of a pigment, and 0 to 5 wt. % of a plasticizer.
10. The polymeric composition of claim 1 , comprising any one of, a combination of, or all of the following properties:
a density of 1 to 1.4 g/cc at 23° C. measured in accordance with ASTM D792;
a tensile modulus equal to or greater than 17000 MPa, or 17000 MPa to 22000 MPa at 23° C., as measured in accordance with ISO 527-1, -2 at 1 mm/min;
a tensile strength at break equal to or greater than 155 MPa, or 155 MPa to 190 MPa at 23° C., as measured in accordance with ISO 527-1, -2 at 5 mm/min;
a tensile elongation at break equal to or greater than 1.1%, at 23° C., as measured in accordance with ISO 527-1, -2 at 5 mm/min; and/or
a flexural modulus greater than 15500 MPa, or 15500 MPa to 19000 MPa at 23° C., as measured in accordance with ISO 178 at 2 mm/min.
11. The polymeric composition of claim 1 , wherein the composition is comprised in a film, a layer, or a sheet.
12. The polymeric composition of claim 1 , wherein the composition is an extruded, blow-molded, injection-molded, rotational molded, compression molded, 3-D printed and/or thermoformed composition.
13. The polymeric composition of claim 1 , wherein the composition is comprised in an article of manufacture.
14. The polymeric composition of claim 13 , wherein the article of manufacture is a computer part.
15. The polymeric composition of claim 13 , wherein the article of manufacture is a desktop computer chassis or chassis part or a laptop computer chassis or chassis part.
16. A computer chassis comprising the polymeric composition of claim 1 .
17. The computer chassis of claim 16 , wherein the computer chassis is a desktop computer chassis, a laptop computer chassis, or a computer tablet chassis.
18. The computer chassis of claim 16 , wherein at least 70 wt. % of the computer chassis comprises recyclable and/or renewable material, wherein the recyclable and/or renewable material comprises plastics and/or carbon fibers.
19. A method of making the computer chassis of claim 16 , the method comprising obtaining the polymeric composition of claim 1 and forming at least a portion of the computer chassis with the polymeric composition.
20. The method of claim 19 , wherein at least 70 wt. % of the computer chassis comprises recyclable and/or renewable material, wherein the recyclable and/or renewable material comprises plastics and/or carbon fibers.