Method for increasing the difference between the melting temperature and the crystallization temperature of a polyamide powder
A method for reducing the crystallization temperature and the melting temperature of a polyamide powder resulting from the polymerization of at least one predominant monomer, in which the reduction in the crystallization temperature is greater than the reduction in the melting temperature, the method including a step of polymerization of the at least one predominant monomer with at least one different minor comonomer polymerized according to the same polymerization process as the at least one predominant monomer, the at least one minor comonomer being chosen from aminocarboxylic acids, diamine/diacid pairs, lactams and/or lactones, and the at least one minor comonomer representing from 0.1% to 20% by weight of the total blend of the monomers(s) and comonomer(s), preferably from 0.5% to 15% by weight of the total blend, preferably from 1% to 10% by weight of the total blend.
1. A process for reducing the crystallization temperature and the melting temperature of a polyamide powder derived from the polymerization of at least one major monomer, said process comprising polymerization of said at least one major monomer with at least one different minor comonomer polymerized according to the same polymerization process as said at least one major monomer, said at least one minor comonomer representing from 0.1% to 20% by mass of the total blend of said monomer(s) and comonomer(s), such that the reduction in the crystallization temperature is greater than the reduction in the melting temperature, relative to the crystallization temperature and the melting temperature of the polyamide obtained from the polymerization of said at least one major monomer alone,
wherein the change in the crystallization temperature is at least 3° C.
2. The process as claimed in claim 1 , wherein said step of polymerization is an anionic polymerization.
3. The process as claimed in claim 1 , wherein said step of polymerization is a hydrolytic polycondensation.
4. The process as claimed in claim 1 , wherein said at least one major monomer is selected from the group consisting of 11-aminoundecanoic acid, lactam 12, decanediamine-sebacic acid couple (10.10) and mixtures thereof.
5. The process as claimed in claim 1 , further comprising, after said polymerization step, at least one step selected from the group consisting of: dissolution, precipitation, extrusion, atomization, spraying, cold nebulization, hot nebulization, milling, cryogenic milling, screening, viscosity raising, and combinations thereof.
6. The process as claimed in claim 1 , wherein the at least one minor comonomer is selected from the group consisting of 11-aminoundecanoic acid, lauryllactam, caprolactam, caprolactone, at least one diamine-diacid couples selected from the group consisting of: 6.6, 6.10, 6.11, 6.12, 6.14, 6.18, 10.10, 10.12, 10.14, 10.18 and 10.T, T being terephthalic acid, and mixtures thereof.
7. The process as claimed in claim 1 , wherein said at least one minor comonomer represents from 0.1% to 12% by mass of the total blend of said monomer(s) and comonomer(s).
8. The process as claimed in claim 1 , wherein said at least one minor comonomer represents from 0.1% to 7% by mass of the total blend of said monomer(s) and comonomer(s).
9. The process as claimed in claim 1 , wherein said at least one minor comonomer represents from 0.1% to 1% by mass of the total blend of said monomer(s) and comonomer(s).
10. The process as claimed in claim 1 , wherein the change in the crystallization temperature is at least 5° C.
11. A copolyamide or copolyesteramide powder obtained from the polymerization of at least two different monomers polymerized according to the same polymerization process, at least one of the monomers being major, at least one of the monomers being minor, said at least one minor monomers representing from 0.1% to 20% by mass of the total blend of said monomer(s), wherein the powder has a crystallization temperature and a melting temperature that are each reduced relative to a crystallization temperature and a melting temperature of a powder obtained from the polymerization of said at least one major monomer,
wherein the reduction in the crystallization temperature is greater than the reduction in the melting temperature,
wherein the change in the crystallization temperature is at least 3° C.
12. The powder as claimed in claim 11 , wherein said at least one major monomer is selected from the group consisting of 11-aminoundecanoic acid, lactam 12, decanediamine-sebacic acid couple (10.10) and mixtures thereof.
13. The powder as claimed in claim 11 , wherein said at least one major monomer comprises 11-aminoundecanoic acid and at least one minor monomer is selected from the group consisting of hexamethylenediamine-adipic acid couple (6.6), lauryllactam, caprolactam, caprolactone and mixtures thereof.
14. The powder as claimed in claim 11 , comprising a lauryllactam major monomer and a minor monomer selected from the group consisting of caprolactam, caprolactone, hexamethylenediamine-adipic acid couple (6.6) and mixtures thereof.
15. The powder as claimed in claim 11 , wherein said at least one minor comonomer represents from 0.1% to 12% by mass of the total blend of said monomer(s) and comonomer(s).
16. The powder as claimed in claim 11 , wherein said at least one minor comonomer represents from 0.1% to 7% by mass of the total blend of said monomer(s) and comonomer(s).
17. The powder as claimed in claim 11 , wherein said at least one minor comonomer represents from 0.1% to 1% by mass of the total blend of said monomer(s) and comonomer(s).
18. The powder as claimed in claim 11 , wherein the change in the crystallization temperature is at least 5° C.
19. A process for manufacturing a polyamide article comprising melt-induced powder aggregation using electromagnetic radiation of the powder of claim 11 .
20. The process as claimed in claim 19 , wherein the at least one minor monomer is selected from the group consisting of 11-aminoundecanoic acid, lauryllactam, caprolactam, caprolactone, and at least one diamine-diacid couple selected from the group consisting of 6.6, 6.10, 6.11, 6.12, 6.14, 6.18, 10.10, 10.12, 10.14, 10.18 and 10.T, T being terephthalic acid.
21. A process for reducing the crystallization temperature and the melting temperature of a polyamide powder derived from a polymerization of at least one major monomer, said process comprising a step of polymerization of said at least one major monomer with at least one different minor comonomer polymerized according to the same polymerization process as said at least one major monomer, wherein said at least one minor comonomer represents from 0.1% to 20% by mass of the total blend of said monomer(s) and comonomer(s), such that the reduction in the crystallization temperature is greater than the reduction in the melting temperature, relative to the crystallization temperature and the melting temperature of the polyamide obtained from the polymerization of said at least one major monomer alone,
wherein the polymerization is an anionic polymerization which includes the use of components selected from the group consisting of a catalyst, an activator, an organic filler, an amide or combinations thereof,
wherein the change in the crystallization temperature is at least 3° C.