Multi-purpose phenol-free direct thermal recording media
Non-phenolic direct thermal recording media have a thermally responsive layer containing a leuco dye and a plurality of non-phenolic developers including 1,3-diphenyl urea (DPU) and urea urethane (UU). This chemistry enables multi-purpose recording materials capable of withstanding multiple different types of environmental conditions or agents—such as a water soak, contact with polyvinyl chloride meat wrapping film, boiling water, dry and humid heat, sunlight, and contact with hand sanitizer. The unique non-phenolic chemistry allows the product's thermally responsive layer to have an ultra-low coat weight, less than 1.48 g/m 2 .
1. A recordable medium, comprising:
a substrate; and
a thermally responsive layer carried by the substrate, the thermally responsive layer including a leuco dye and a plurality of developers;
wherein the recording medium is substantially phenol-free;
wherein the plurality of developers include 1,3-Diphenyl urea (DPU) and a urea urethane having the CAS No. 321860-75-7 (UU);
wherein the DPU and the UU are present in the thermally responsive layer in a relative weight ratio that falls within a range from ⅓ to 3;
wherein the thermally responsive layer has a coat weight of less than or equal to 1.3 g/m 2 and at least 0.9 g/m 2 ; and wherein a print quality of the recording medium when printed is characterized by an ANSI value of at least 1.5 after the printed recording medium is heated to 60° C. for at least 24 hours, then removed and cooled.
2. The medium of claim 1 , further comprising:
a basecoat layer between the thermally responsive layer and the substrate.
3. The medium of claim 1 , further comprising:
a topcoat carried by the substrate such that the thermally responsive layer is disposed between the topcoat and the substrate.
4. The medium of claim 1 , wherein the DPU and the UU are dispersed throughout the thermally responsive layer.
5. The medium of claim 1 , wherein no developers other than DPU and UU are present in the thermally responsive layer.
6. The medium of claim 1 , wherein the DPU and the UU are present in the thermally responsive layer in a relative weight ratio that falls within a range from 1:1 to 3:1.
7. The medium of claim 6 , wherein the relative weight ratio falls within a range from ½ to 2.
8. The medium of claim 7 , wherein the relative weight ratio is 1.
9. The medium of claim 1 , wherein a print quality of the recording medium when printed with a thermal printer energy setting of 11.7 mJ/mm 2 at a print speed of 6 inches per second (ips) is characterized by an ANSI value of at least 1.5.
10. The medium of claim 9 , wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 after the printed recording medium is soaked in water for 24 hours and then removed and dried.
11. The medium of claim 9 , wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 after the printed recording medium is dipped in water, then placed in contact with polyvinyl chloride meat wrapping film under a 7 pound weight for 24 hours, and then removed and dried.
12. The medium of claim 9 , wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 after the printed recording medium is submerged in boiling water for 20 minutes, then removed and dried.
13. The medium of claim 9 , wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 after the printed recording medium is exposed to air at 40° C. and 90% relative humidity for 24 hours, then removed and cooled.
14. The medium of claim 9 , wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 after the printed recording medium is subjected to an accelerated sunlight test at 0.67 W/m 2 for 7 hours, then removed.
15. The medium of claim 11 , wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 after one drop of a 70% ethyl alcohol-based hand sanitizer is placed on the printed recording medium and allowed to dry.
16. A substantially phenol-free recording medium, comprising:
a flexible substrate; and
a thermally responsive layer carried by the substrate, the thermally responsive layer including a leuco dye and a plurality of developers;
wherein the plurality of developers include 1,3-Diphenyl urea (DPU) and a urea urethane having the CAS No. 321860-75-7 (UU);
wherein the DPU and the UU are both dispersed throughout the thermally responsive layer;
wherein the DPU and the UU are present in the thermally responsive layer in a relative weight ratio that falls within a range from ⅓ to 3;
wherein the thermally responsive layer has a coat weight of less than or equal to 1.3 g/m 2 and at least 0.9 g/m 2 ;
wherein a print quality of the recording medium when printed with a thermal printer energy setting of 11.7 mJ/mm 2 at a print speed of 6 inches per second (ips) is characterized by an ANSI value of at least 1.5; and wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 after the printed recording medium is heated to 60° C. for at least 24 hours, then removed and cooled.
17. The medium of claim 16 ,
wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 after the printed recording medium is dipped in water, then placed in contact with polyvinyl chloride meat wrapping film under a 7 pound weight for 24 hours, and then removed and dried; and
wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 after the printed recording medium is exposed to air at 40° C. and 90% relative humidity for 24 hours, then removed and cooled.
18. The medium of claim 16 , wherein the DPU and the UU are present in the thermally responsive layer in a relative weight ratio that falls within a range from 1:1 to 3:1.