Soft magnetic alloy, soft magnetic alloy ribbon, method of manufacturing soft magnetic alloy ribbon, magnetic core, and component
The soft magnetic alloy of the present disclosure is represented by a composition formula of Fe a Si b B c Cu d M e where M is at least one type of element selected from a group consisting of Nb, Mo, V, Zr, Hf, and W, and the formula satisfies 82.5≤a≤86, 0.3≤b≤3, 12.5≤c≤15.0, 0.05≤d≤0.9, and 0≤e<0.4 in at %. The soft magnetic alloy includes a structure that has a crystal grain with a grain diameter of 60 nm or less in an amorphous phase.
1. A soft magnetic alloy ribbon including an alloy represented by a composition formula of Fe a Si b B c Cu d M e , M being at least one type of element selected from a group consisting of Nb, Mo, V, Zr, Hf, and W, and the formula satisfying 82.5≤a≤86, 0.3≤b≤3, 12.5≤c≤15.0, 0.05≤d≤0.9, and 0≤e<0.4 in at %, the soft magnetic alloy ribbon comprising:
a structure that has a crystal grain with a grain diameter of 60 nm or less in an amorphous phase,
wherein a saturation magnetic flux density of the soft magnetic alloy ribbon is 1.75 T or more,
wherein an iron loss of the soft magnetic alloy ribbon at 1 kHz and at 1 T is 25 W/kg or less, and
wherein a lamination factor of the soft magnetic alloy ribbon is 86% or more.
2. The soft magnetic alloy ribbon according to claim 1 ,
wherein a density of the soft magnetic alloy ribbon is 7.45 g/cm 3 or more.
3. The soft magnetic alloy ribbon according to claim 1 ,
wherein a thickness of the soft magnetic alloy ribbon is 25 μm or more.
4. The soft magnetic alloy ribbon according to claim 1 ,
wherein a magnetic flux density of the soft magnetic alloy ribbon when a magnetic field of 80 A/m is imposed in a casting direction of the soft magnetic alloy ribbon is a magnetic flux density L, and a magnetic flux density of the soft magnetic alloy ribbon when a magnetic field of 80 A/m is imposed in a direction orthogonal to the casting direction of the soft magnetic alloy ribbon is a magnetic flux density W, and
wherein a ratio (L/W) of the magnetic flux density L to the magnetic flux density W is from 0.7 to 1.3.
5. The soft magnetic alloy ribbon according to claim 1 ,
wherein a saturation magnetostriction of the soft magnetic alloy ribbon is 20 ppm or less.
6. The soft magnetic alloy ribbon according to claim 1 ,
wherein the formula satisfies 83≤a≤86, 0.3≤b≤2, 0.4≤d≤0.9, and 0≤e≤0.3, and
wherein a saturation magnetic flux density of the soft magnetic alloy ribbon is 1.77 T or more.
7. The soft magnetic alloy ribbon according to claim 1 ,
wherein a part of Fe content is replaced with at least one type of element selected from Co and Ni up to 6 at % at a maximum.
8. A magnetic core formed by using the soft magnetic alloy ribbon according to claim 1 .
9. A component comprising the magnetic core according to claim 8 , and a coil.
10. A method of manufacturing the soft magnetic alloy ribbon of claim 1 , the method comprising:
ejecting a molten alloy on a rotating chill roll; and
quenching the molten alloy on the chill roll,
wherein an outer circumferential portion of the chill roll is made of a Cu alloy having a thermal conductivity of 120 W/(m·K) or more.