Battery separator configured for reducing acid stratification for enhanced flooded batteries
A battery separator configured for reducing acid stratification for an enhanced flooded battery. The battery separator for the enhanced flooded battery is configured to minimize acid stratification. The battery separator is comprised of a microporous membrane and an absorptive mat. The absorptive mat includes a 3-hour wicking height greater than 15 cm. Wherein the absorptive mat of the battery separator is configured to minimize acid stratification of the enhanced flooded battery.
1. A battery separator for an enhanced flooded battery comprising:
a microporous membrane; and
an absorptive mat configured with an ability to swell when wetted and thus increase a thickness, whereby, the absorptive mat includes a 3-hour wicking height greater than 15 cm, wherein, the absorptive mat is configured to minimize acid stratification of the enhanced flooded battery.
2. The battery separator of claim 1 , wherein the absorptive mat including:
the 3-hour wicking height of the absorptive mat is greater than 25 cm; or
the 3-hour wicking height of the absorptive mat is greater than 35 cm;
wherein, a material wicking height of the absorptive mat is at least 50 mm in 2 minutes.
3. The battery separator of claim 2 , wherein the wicking height of the absorptive mat is at least 50 mm in 1 minute, wherein:
when the absorptive mat has a Brunauer-Emmett-Teller (“BET”) of 0.9 m2/gram, the material wicking height of the absorptive mat is:
64 mm at 1 minute;
89 mm at 2 minutes;
125 mm at 5 minutes; and
257 mm at 30 minutes;
when the absorptive mat has a BET of 1.3 m2/gram, the material wicking height of the absorptive mat is:
55 mm at 1 minute;
74 mm at 2 minutes;
112 mm at 5 minutes; and
236 mm at 30 minutes;
when the absorptive mat has a Brunauer-Emmett-Teller (“BET”) of 0.9 m2/gram, the material wicking height of the absorptive mat is:
10 cm at 7 minutes;
32 cm in 2 hours; and
39 cm in 3 hours;
or
when the absorptive mat has a BET of 1.3 m2/gram, the material wicking height of the absorptive mat is:
10 cm at 9 minutes;
30 cm in 2 hours; and
37 cm in 3 hours.
4. The battery separator of claim 1 , wherein the thickness of the absorptive mat is less than 1.0 mm.
5. The battery separator of claim 4 , wherein the thickness of the absorptive mat is less than 0.5 mm.
6. The battery separator of claim 1 , wherein the absorptive mat including microfibers, where at least 10% of the absorptive mat are fibers having a diameter of less than 1 micrometer, the microfibers of the absorptive mat include glass microfibers, polymeric microfibers, or a combination thereof.
7. The battery separator of claim 6 , wherein the microfibers of the absorptive mat consist of the glass microfibers, the polymeric microfibers, or the combination thereof.
8. The battery separator of claim 1 , where the microporous membrane is primarily flat, wherein the microporous membrane has no primary ribs.
9. The battery separator of claim 8 wherein the primarily flat microporous membrane including:
mini-ribs, where the mini-ribs are on one side or both sides of the microporous membrane, wherein the mini-ribs have a height of 0.1 mm, 0.3 mm, or a combination thereof;
an embossed texture on one side or both sides of the microporous membrane, where the embossed texture resembles 100 grit sand-paper; or
a combination thereof.
10. The battery separator of claim 1 , wherein the absorptive mat is on both sides of the microporous membrane.
11. The battery separator of claim 1 further comprising a non-absorptive glass mat, wherein the microporous membrane and the absorptive mat are separated by and laminated to the non-absorptive glass mat.
12. The battery separator of claim 1 , wherein the enhanced flooded battery is a flooded automotive lead-acid battery that has free acid that is prone to acid stratification under start-stop operation, where the flooded automotive lead-acid battery is not sealed, wherein the flooded automotive lead-acid battery is configured to allow water to be added post-production.
13. A battery separator for an enhanced flooded battery comprising:
a primarily flat microporous membrane including no primary ribs, the primarily flat microporous membrane includes:
mini-ribs on one or both sides of the primarily flat microporous membrane, the mini-ribs have a height of 0.1 mm, 0.3 mm, or a combination thereof; and
an absorptive mat configured with an ability to swell when wetted and thus increase a thickness, whereby, the absorptive mat includes a 3-hour wicking height greater than 15 cm, the absorptive mat includes at least 10% of microfibers having a diameter of less than 1 micrometer, wherein the microfibers of the absorptive mat include a combination of glass microfibers and polymeric microfibers, the absorptive mat has a thickness of less than 1.0 mm;
wherein the absorptive mat is configured to minimize acid stratification of the enhanced flooded battery.
14. The battery separator of claim 13 further comprising:
a non-absorptive glass mat, wherein the microporous membrane and the absorptive mat are separated by and laminated to the non-absorptive glass mat; and
the absorptive mat is on both sides of the microporous membrane.
15. Battery separator of claim 13 , wherein:
the enhanced flooded battery is a flooded automotive lead-acid battery that has free acid that is prone to acid stratification under start-stop operation, where the flooded automotive lead-acid battery is not sealed, wherein the flooded automotive lead-acid battery is configured to allow water to be added post-production; and
wherein a material-wicking height of the absorptive mat is at least 50 mm in 2 minutes.
16. The battery separator of claim 13 , wherein:
the 3-hour wicking height of the absorptive mat is greater than 25 cm; or
the 3-hour wicking height of the absorptive mat is greater than 35 cm;
wherein, a material wicking height of the absorptive mat is at least 50 mm in 2 minutes.
17. An enhanced flooded battery comprising:
a battery separator configured for the enhanced flooded battery, the battery separator comprising:
a microporous membrane; and
an absorptive mat, the absorptive mat includes a 3-hour wicking height greater than 15 cm;
wherein the absorptive mat of the battery separator is configured to minimize acid stratification of the enhanced flooded battery.
18. The enhanced flooded battery of claim 17 , wherein:
the microporous membrane is primarily flat including no primary ribs, the primarily flat microporous membrane includes:
mini-ribs on one or both sides of the primarily flat microporous membrane, the mini-ribs have a height of 0.1 mm, 0.3 mm, or a combination thereof; and
the absorptive mat including microfibers having a diameter of less than 1 micrometer, the absorptive mat including at least 10% of said microfibers, the microfibers of the absorptive mat include glass microfibers, polymeric microfibers, or a combination thereof;
the absorptive mate has a thickness of less than 1.0 mm;
wherein the material wicking height of the absorptive mat is at least 50 mm in 2 minutes;
wherein the absorptive mat is configured to minimize acid stratification of the enhanced flooded battery;
wherein the battery separator further comprising:
a non-absorptive glass mat, wherein the microporous membrane and the absorptive mat are separated by and laminated to the non-absorptive glass mat; and
the absorptive mat is on both sides of the microporous membrane;
the enhanced flooded battery is a flooded automotive lead-acid battery that has free acid that is prone to acid stratification under start-stop operation, where the flooded automotive lead-acid battery is not sealed, wherein the flooded automotive lead-acid battery is configured to allow water to be added post-production.