System, apparatus, and methods for managing sintering supports
Systems, apparatus and methods of additively manufacturing objects are disclosed. Specifically, provided herein are methods of heating objects having a particle-based support at least partially surrounding the object during portions of stages of the heating. Additionally, systems, apparatus, and methods for removing the particle-based support during heating, such that the object can continue heating to form a final part. Systems, apparatus, and methods for distributing the particle-based support to shore the objects through heating are disclosed. Systems, apparatus, and methods for removing the particle-based support are also disclosed herein.
1. A method of additively manufacturing a three-dimensional object, comprising steps of:
providing a part comprising a model material and one or more binder components within a volume of a heating apparatus;
adding a particle-based support to the volume such that the part is at least partially surrounded, the particle-based support comprising a pliable particle based support;
heating the part to a first temperature to form a pre-sintered object that possesses at least sufficient strength to retain its printed shape without the particle-based support; and
removing the particle-based support from about the pre-sintered object.
2. The method of claim 1 , further comprising heating the pre-sintered object to a second temperature such that a densified three-dimensional object is formed.
3. The method of claim 1 , wherein heating to the first temperature includes forming necks to connect neighboring particle surfaces of the model material.
4. The method of claim 3 , further comprising fluidizing the particle-based support around the part such that the particle-based support provides a buoyant force to the part.
5. The method of claim 4 , wherein fluidizing the particle-based support occurs following the onset of the necks connecting neighboring particle surfaces of the model material.
6. The method of claim 1 , wherein the model material comprises sinterable particles.
7. The method of claim 6 , wherein the first temperature is an initial sintering temperature of the model material.
8. The method of claim 1 , wherein the model material is characterized by a melting temperature that is lower than a melting temperature of the particle-based support.
9. The method of claim 1 , wherein adding the particle-based support includes depositing the particle-based support in the volume such that the particle-based support at least partially surrounds the part to fill gaps, overhangs, cantilevered portions, and/or unsupported ranges or spans of the part.
10. The method of claim 9 , further comprising supporting, with the particle based support, the cantilevered portions, gaps, overhangs, and/or unsupported ranges or spans of the part against deformation.
11. The method of claim 10 , wherein supporting the cantilevered portions, gaps, overhangs, and/or unsupported ranges or spans of the part against deformation includes supporting against sagging, slumping with gravity under a weight of the part, or combinations thereof.
12. The method of claim 9 , wherein the depositing comprises at least one of pouring, spreading, or rolling.
13. The method of claim 12 , wherein the depositing further comprises vibrating or shaking the volume.
14. The method of claim 9 , wherein depositing the particle-based support permits the particle-based support to occupy a volume between a surface of a build chamber and an opposing unsupported surface of the part or occupy a volume between a supported surface of model material and an opposing unsupported surface of model material.
15. The method of claim 9 , wherein heating to the first temperature results in the crumbling of the particle-based support between the pre-sintered object's cantilevered portions, gaps, overhangs, and/or unsupported ranges or spans when pressure is applied by the pre-sintered object at about the first temperature.
16. The method of claim 1 , wherein the model material comprises metal particles.
17. The method of claim 1 , wherein the one or more binder components comprises a polymer-based binder.
18. The method of claim 1 , wherein the particle-based support is a ceramic.
19. The method of claim 1 , further comprising applying a flow of gas to the particle-based support at a flow rate lower than a force needed to fluidize the particle-based support.
20. The method of claim 19 , wherein the flow of gas is applied to the particle-based support during heating to the first temperature.
21. The method of claim 1 , wherein removing the particle-based support comprises vacuuming the particle-based support out of the volume.
22. The method of claim 1 , wherein removing the particle-based support further comprises vibrating the particle-based support from about the pre-sintered object.
23. The method of claim 1 , wherein removing the particle-based support further comprises propelling the particle-based support from about the pre-sintered object.
24. The method of claim 23 , wherein propelling the particle-based support comprises applying a compressed gas to the particle-based support.
25. The method of claim 1 , further comprising receiving, with holes and/or ports positioned in a base of the volume, used particle-based support.
26. The method of claim 25 , further comprising collecting, using a secondary chamber, receptacle, repository, or cistern positioned beneath or adjacent to the volume and in communication with the holes and/or ports positioned in the base of the volume, used particle-based support.
27. The method of claim 1 , wherein the heating to the first temperature includes softening the pliable particle-based support such that it compresses between the cantilevered portions, gaps, overhangs, and/or unsupported ranges or spans of the pre-sintered object when pressure is applied by the pre-sintered object at about the first temperature.
28. A method of additively manufacturing a three-dimensional object, comprising steps of:
providing a part comprising a model material and one or more binder components within a volume of a heating apparatus;
adding a particle-based support to the volume such that the part is at least partially surrounded;
heating the part to a first temperature to form a pre-sintered object that possesses at least sufficient strength to retain its printed shape without the particle-based support, where heating to the first temperature results in the evaporation of the particle-based support; and
removing the particle-based support from about the pre-sintered object.
29. A method of additively manufacturing a three-dimensional object, comprising steps of:
providing a part comprising a model material and one or more binder components within a volume of a heating apparatus;
adding a particle-based support to the volume such that the part is at least partially surrounded;
heating the part to a first temperature to form a pre-sintered object that possesses at least sufficient strength to retain its printed shape without the particle-based support, where heating to the first temperature results in the sublimation of the particle-based support; and
removing the particle-based support from about the pre-sintered object.
30. A method of additively manufacturing a three-dimensional object, comprising steps of:
providing a part comprising a model material and one or more binder components within a volume of a heating apparatus;
adding a particle-based release material to the volume such that the part is at least partially surrounded;
heating the part to a first temperature to form a pre-sintered object that possesses at least sufficient strength to retain its printed shape without the particle-based release material, the particle-based release material powderizing when heated to the first temperature to reduce stress in the pre-sintered object during sintering; and
removing the particle-based release material from about the pre-sintered object.