Crystalline microporous germanosilicates of cit-13 topology and methods of preparing and using the same
The present disclosure is directed to novel germanosilicate compositions and methods of producing the same. In particular, this disclosure describes new silica-rich compositions of the germanosilicate designated CIT-13, with and without added metal oxides. The disclosure also describes methods of preparing and using these new germanosilicate compositions as well as the compositions themselves.
1. A crystalline microporous germanosilicate of CIT-13 topology having a three-dimensional framework having pores defined by 10- and 14-membered rings and an Si:Ge ratio in a range of from 25 to 250.
2. The crystalline microporous germanosilicate of CIT-13 topology of claim 1 , that exhibits a powder X-ray diffraction pattern (PXRD) exhibiting at least five of the characteristic peaks at 6.70±0.2, 7.34±0.2, 12.85±0.2, 18.25±0.2, 18.35±0.2, 18.63±0.2, 20.78±0.2, 21.55±0.2, 23.35±0.2, 24.55±0.2, 26.01±0.2, and 26.68±0.2 degrees 2-θ.
3. The crystalline microporous germanosilicate of CIT-13 topology of claim 1 , further comprising one or more lattice oxides of metal, M, wherein M is Al, B, Fe, Ga, Hf, Sn, Ti, V, Zn, Zr, or a combination thereof, and M is present in the CIT-13 lattice with a Si/M ratio in a range of from 15 to 250.
4. The crystalline microporous germanosilicate of CIT-13 topology of claim 3 , wherein the Si/M ratio is in a range of from 25 to 250.
5. The crystalline microporous germanosilicate of CIT-13 topology of claim 3 , wherein M is Al, B, Fe, Sn, Ti, and/or Zn.
6. The crystalline microporous germanosilicate of CIT-13 topology of claim 3 , comprising an oxide of Al, that exhibits an 27 Al MAS NMR spectrum having a characteristic chemical shift at about 54 ppm, relative to 1 M aqueous aluminum nitrate solution, and a 29 Si MAS NMR spectrum having characteristic chemical shifts at about −110 ppm and −115 ppm, relative to tetramethylsilane (TMS).
7. The crystalline microporous germanosilicate of claim 3 , in its hydrogen form.
8. The crystalline microporous germanosilicate of claim 3 , comprising micropores optionally containing a metal cation salt, a transition metal, a transition metal oxide, or a transition metal salt in its micropores.
9. The crystalline microporous germanosilicate of claim 3 , comprising micropores containing a metal cation salt, a transition metal, a transition metal oxide, or a transition metal salt in its micropores.
10. The crystalline microporous germanosilicate of CIT-13 topology of claim 1 , prepared by treating a hydrothermally prepared crystalline microporous germanosilicate of CIT-13 topology having a Si/Ge ratio in a range of from 4.5 to 10, with a concentrated mineral acid at an elevated temperature.
11. The crystalline microporous germanosilicate of CIT-13 topology of claim 1 , prepared by treating a crystalline microporous germanosilicate of CIT-13 topology having a Si/Ge ratio in a range of from 4.5 to 10, with nitric acid having a concentration in a range of from 0.9 M to 1.1 M at a temperature in a range of from 160° C. to 230° C.
12. The crystalline microporous germanosilicate of CIT-13 topology of claim 11 , wherein the crystalline microporous germanosilicate of CIT-13 topology having a Si/Ge ratio in a range of from 4.5 to 10 is prepared hydrothermally.
13. The crystalline microporous germanosilicate of CIT-13 topology of claim 1 , prepared by treating a crystalline microporous germanosilicate of CIT-13 topology having a Si/Ge ratio in a range of from 4.5 to 10, with a concentrated mineral acid at an elevated temperature, in the presence of a source of the corresponding one or more oxides of metal, M, wherein M is Al, B, Fe, Ga, Hf, Sn, Ti, V, Zn, Zr, or a combination thereof.
14. The crystalline microporous germanosilicate of claim 1 , in its hydrogen form.
15. The crystalline microporous germanosilicate of claim 1 , comprising micropores optionally containing a metal cation salt, a transition metal, a transition metal oxide, or a transition metal salt in its micropores.
16. A process for affecting a chemical transformation or separation, the process comprising:
(a) carbonylating DME with CO at low temperatures;
(b) reducing NOx with methane:
(c) cracking, hydrocracking, or dehydrogenating a hydrocarbon;
(d) dewaxing a hydrocarbon feedstock;
(e) converting paraffins to aromatics:
(f) isomerizing or disproportionating an aromatic feedstock;
(g) alkylating an aromatic hydrocarbon;
(h) oligomerizing an alkene;
(i) aminating a lower alcohol;
(j) separating and sorbing a lower alkane from a hydrocarbon feedstock;
(k) isomerizing an olefin;
(l) producing a higher molecular weight hydrocarbon from lower molecular weight hydrocarbon;
(m) reforming a hydrocarbon
(n) converting a lower alcohol or other oxygenated hydrocarbon to produce an olefin product;
(o) epoxidizing olefins with hydrogen peroxide;
(p) reducing the content of an oxide of nitrogen contained in a gas stream in the presence of oxygen;
(q) separating nitrogen from a nitrogen-containing gas mixture; or
(r) converting synthesis gas containing hydrogen and carbon monoxide to a hydrocarbon stream; or
(s) reducing the concentration of an organic halide in an initial hydrocarbon product;
by contacting a respective feedstock with the crystalline microporous germanosilicate of claim 15 , under conditions sufficient to affect the named chemical transformation or separation.
17. The crystalline microporous germanosilicate of claim 1 , comprising micropores containing a metal cation salt, a transition metal, a transition metal oxide, or a transition metal salt in its micropores.
18. A method of preparing the crystalline microporous germanosilicate of CIT-13 topology of claim 1 , the method comprising treating a precursor crystalline microporous germanosilicate of CIT-13 topology having a Si/Ge ratio in a range of from 4.5 to 10 with a concentrated mineral acid under conditions sufficient to degermanate at least a portion of the CIT-13 germanosilicate, so as to produce a CIT-13 germanosilicate with a Si/Ge ratio in a range of from 25 to 250.
19. The method of claim 14 , wherein the precursor crystalline microporous germanosilicate of CIT-13 topology having a Si/Ge ratio in a range of from 4.5 to 10 has been prepared hydrothermally.
20. The method of claim 18 , further comprising subjecting the crystalline microporous germanosilicate of CIT-13 topology having a Si/Ge ratio in a range of from 4.5 to 10 to concentrated mineral acid in the presence of a source of a metal or metalloid oxide, M, where M is aluminum, boron, gallium, hafnium, iron, tin, titanium, vanadium, zinc, zirconium, or combination thereof, under conditions sufficient to degermanate at least a portion of the CIT-13 germanosilicate, so as to produce a crystalline microporous germanosilicate of CIT-13, having an Si/Ge ratio in a range of from 25 to 250 and comprising one or more lattice oxides of metal, M, having an Si/M ratio in a range of from 15 to 250.