Germanosilicate compositions of CIT-14 topology and methods of preparing and using the same
The present disclosure is directed to novel germanosilicate compositions and methods of producing and using the same. In particular, this disclosure describes new germanosilicates of CIT-14 topology. The disclosure also describes methods of preparing and using these new germanosilicate compositions as well as the compositions themselves.
1. A crystalline microporous germanosilicate designated CIT-14 having a three-dimensional framework with channel pores defined by 8- and 12-membered rings and having an Si:Ge ratio in a range of from 25 to practically infinity.
2. The crystalline microporous germanosilicate of claim 1 , which exhibits one or both of:
(a) a powder X-ray diffraction (XRD) pattern exhibiting at least five of the characteristic peaks at 7.55±0.2, 8.06±0.2, 12.79±0.2, 18.82±0.2, 19.04±0.2, 20.67±0.2, 22.07±0.2, 24.36±0.2, 27.01±0.2, and 27.48±0.2 degrees 2-θ; or
(b) a powder X-ray diffraction (XRD) pattern substantially the same as shown in FIG. 32 or 33 (A).
3. The crystalline microporous germanosilicate of claim 1 having an Si:Ge ratio in a range of from 25 to 150.
4. The crystalline microporous germanosilicate of claim 1 that exhibits a powder X-ray diffraction pattern having at least five of the characteristic peaks at 7.55±0.2, 8.06±0.2, 12.79±0.2, 18.82±0.2, 19.04±0.2, 20.67±0.2, 22.07±0.2, 24.36±0.2, 27.01±0.2, and 27.48±0.2 degrees 2-θ.
5. The crystalline microporous germanosilicate of claim 1 , that exhibits a 29 Si MAS NMR spectrum exhibiting multiple Q4 Si environments within the −108 to −120 chemical shift regions.
6. The crystalline microporous germanosilicate of claim 1 , prepared by treating a phyllosilicate designated CIT-13P comprising delaminated silica rich cfi-layers and having a Si:Ge ratio in a range of from 40 to infinity with a source of silica in the presence of a concentrated mineral acid at an elevated temperature to form an alkoxylated intermediate composition that is isolated and calcined.
7. The crystalline microporous germanosilicate of claim 6 , wherein:
(a) the concentrated mineral acid is aqueous HCl or HNO 3 in a concentration in a range of from 1 M to 1.5 M; and/or
(b) the source of silica is diethoxydimethylsilane (DEDMS) and/or 1,3-diethoxy-1,1,3,3-tetramethyldisiloxane (DETMDS); and/or
(c) the elevated temperature is a temperature in a range of from 165° C. to 225° C.
8. The crystalline microporous germanosilicate of claim 1 , in its hydrogen form.
9. The crystalline microporous germanosilicate of claim 1 , comprising micropores optionally containing a metal cation salt, a transition metal, a transition metal oxide, or a transition metal salt in its micropores.
10. A process for affecting a chemical transformation or separation, the process comprising:
(a) carbonylating DME with CO at low temperatures;
(b) reducing NOx with methane:
(c) cracking, hydrocracking, or dehydrogenating a hydrocarbon;
(d) dewaxing a hydrocarbon feedstock;
(e) converting paraffins to aromatics:
(f) isomerizing or disproportionating an aromatic feedstock;
(g) alkylating an aromatic hydrocarbon;
(h) oligomerizing an alkene;
(i) aminating a lower alcohol;
(j) separating and sorbing a lower alkane from a hydrocarbon feedstock;
(k) isomerizing an olefin;
(l) producing a higher molecular weight hydrocarbon from lower molecular weight hydrocarbon;
(m) reforming a hydrocarbon
(n) converting a lower alcohol or other oxygenated hydrocarbon to produce an olefin product (including MTO);
(o) epoxidizing olefins with hydrogen peroxide;
(p) reducing the content of an oxide of nitrogen contained in a gas stream in the presence of oxygen;
(q) separating nitrogen from a nitrogen-containing gas mixture; or
(r) converting synthesis gas containing hydrogen and carbon monoxide to a hydrocarbon stream; or
(s) reducing the concentration of an organic halide in an initial hydrocarbon product; by contacting the respective feedstock with a crystalline microporous germanosilicate of claim 9 , under conditions sufficient to affect the named transformation.
11. The crystalline microporous germanosilicate of claim 1 , comprising micropores containing a metal cation salt, a transition metal, a transition metal oxide, or a transition metal salt in its micropores.
12. A method of preparing the crystalline microporous germanosilicate of claim 1 , the method comprising treating the crystalline phyllosilicate designated CIT-13P comprising delaminated silica rich cfi-layers and having a Si:Ge ratio in a range of from 40 to infinity with a concentrated mineral acid in the presence of a silica source under conditions to form an alkoxylated intermediate, followed by calcining the alkoxylated intermediate under conditions sufficient to form a CIT-14 germanosilicate.
13. The method of claim 10 , wherein:
(a) the concentrated mineral acid is aqueous HCl or HNO 3 in a concentration in a range of from 1 M to 1.5 M; and/or
(b) the source of silica is diethoxydimethylsilane (DEDMS) and/or 1,3-diethoxy-1,1,3,3-tetramethyldisiloxane (DETMDS); and/or
(c) the elevated temperature is a temperature in a range of from 165° C. to 225° C.