Composition containing a novolac
The invention relates to a composition containing a novolak and water. In one embodiment, a composition is provided comprising novolak and water with the percentage of ortho linkages of the phenol rings of the novolak is greater than that of para linkages, the novolak having a phenolic compound and an aldehyde molar ratio of from 1:0.2 to 1:0.45 and the composition having from 2% to 20% by weight of water based on the weight of the sum of the novolak and the water.
1. A homogenous novolak composition comprising:
a novolak and
3.48 wt % to about 10 wt % water based on the total weight of the novolac and water, wherein:
a percentage of ortho linkages of phenol rings of the novolak is greater than that of para linkages of the phenol rings of the novolak,
the novolak has a phenolic compound to aldehyde molar ratio of from 1:0.25 to 1:0.4; and
the composition has a viscosity of from 1,000 mPa*s to 5,000 mPa*s at 60° C., as determined by ISO 2884 1, and wherein the composition is a homogeneous liquid phase solution at a temperature of from 20° C. to 80° C.
2. The composition according to claim 1 , wherein the composition contains about 10 wt % of water based on the total weight of the novolak and the water.
3. The composition according to claim 1 , wherein the composition contains from 7 wt % to about 10 wt % of water based on the total weight of the novolak and the water.
4. The composition according to claim 2 , wherein the molar ratio of the phenolic compound to the aldehyde is from 1:0.3 to 1:0.4.
5. The composition according to claim 1 , comprising one or more solvents.
6. The composition according to claim 5 , wherein the solvent is selected from the group consisting of triethyl phosphate, tris(chloropropyl)phosphate, benzyl alcohol, dibasic esters, diethylene glycol and ethylene glycol and combinations thereof.
7. The composition according to claim 6 , wherein the solvent is diethylene glycol.
8. The composition according to claim 7 , wherein the solvent is present in a concentration of from 1 to 10% by weight based on all components of the composition.
9. The composition according to claim 1 , wherein the composition does not contain a protective colloid.
10. A process for producing a composition comprising a novolak and water, comprising:
a) producing a novolak comprising a percentage of the ortho linkages of the phenol rings is greater than that of the para linkages by condensation of a phenolic compound and an aldehyde in a ratio of from 1:0.25 to 1:0.4,
b) mixing of the condensate produced under a) with from 3.48 wt % to about 10 wt % of water based on the total weight of the novolak and the water at temperatures in the range from 80 to 100° C. to produce a composition comprising the novolak and water, wherein the composition has a viscosity of from 1,000 mPa*s to 5,000 mPa*s at 60° C., as determined by ISO 2884 1, and the composition is a homogeneous liquid phase solution at a temperature of from 20° C. to 80° C.
11. A novolak polyol comprising the composition of claim 1 .
12. The process according to claim 10 , further comprising reacting the composition with one or more alkylene oxides, alkylene carbonates, or combinations thereof.
13. The composition according to claim 5 , wherein the solvent is selected from the group consisting of diols, glycols ethers and combinations thereof.
14. The process according to claim 12 , wherein the one or more alkylene oxides are selected from the group consisting of ethylene oxide, propylene oxide, butylene oxide, and combinations thereof, and wherein the alkylene carbonates are selected from the group consisting of ethylene carbonate, propylene carbonate, butylene carbonates, and combinations thereof.
15. A homogenous novolak composition comprising:
a novolak having a molar ratio of phenolic compound to aldehyde of from 1:0.25 to 1:0.4, wherein a percentage of ortho linkages of the phenol rings is greater than that of para linkages;
1 to 10% by weight of a solvent selected from the group consisting of triethyl phosphate, tris(chloropropyl)phosphate, benzyl alcohol, dibasic esters, diethylene glycol and ethylene glycol and combinations thereof, based on total weight of the composition; and
3.48 wt % to about 10 wt % water based on the total weight of the novolac and water,
wherein the composition does not contain a protective colloid, and
wherein the composition has a viscosity of from 1,000 mPa*s to 5,000 mPa*s at 60° C., as determined by ISO 2884 1, and the composition is a homogeneous liquid phase solution at a temperature of from 20° C. to 80° C.
16. The composition according to claim 15 , wherein the solvent is diethylene glycol.
17. The composition according to claim 1 , wherein the composition is a homogeneous liquid phase solution at a temperature of from 20° C. to 60° C.
18. The composition according to claim 15 , wherein the composition is a homogeneous liquid phase solution at a temperature of from 20° C. to 60° C.
19. The composition according to claim 1 , wherein the composition has a number average molecular weight (Mn) of 210-400 g/mol.