Composite formed of cubic boron nitride without Ti-based ceramide and method of making thereof
A cubic boron nitride (cBN)-based composite including about 30-65 vol. % cBN, about 3-30 vol. % zirconium (Zr)-containing compounds, about 0-10 vol. % cobalt-tungsten-borides (Co x W y B z ), about 2-30 vol. % aluminum oxide (Al 2 O 3 ), about 0.5-10 vol. % tungsten borides, and less than or equal to about 5 vol. % aluminum nitride (AlN).
1. A cubic boron nitride (cBN)-based composite, consisting of:
about 30-65 vol. % cBN;
about 3-30 vol. % zirconium (Zr)-containing compounds comprising at least zirconium carbo-nitride (ZrCN) or zirconium diboride (ZrB 2 );
about 0-10 vol. % cobalt-tungsten-borides (Co x W y B z );
about 2-30 vol. % aluminum oxide (Al 2 O 3 );
about 0.5-10 vol. % tungsten borides; and
less than or equal to about 5 vol. % aluminum nitride (AlN), wherein the cBN-based composite excludes Ti-containing compounds.
2. The cBN-based composite of claim 1 , wherein the Co x W y B z is selected from the group consisting of crystalline CoWB, crystalline CoW 2 B 2 , and crystalline CoW 3 B 3 .
3. The cBN-based composite of claim 1 , wherein the Co x W y B z excludes W 2 Co 21 B 6 .
4. A cutting tool for cutting superalloys, comprising the cBN-based composite of claim 1 .
5. The cBN-based composite of claim 1 , wherein the cBN has a grain size of about 0.1 micrometer (μm)-4 μm.