Method of recycling used printing plates
A method of producing a granulated product from photopolymer printing plate materials. The method includes the steps of (a) sorting the photopolymer printing plate materials based on an identifiable property, wherein the photopolymer printing plate materials comprise one or more photopolymer layers; (b) grinding the photopolymer printing plate materials to particles; and (c) screening the particles to remove particles above a certain size and create the granulated product.
1. A method of producing a granulated product from photopolymer printing plate materials, the method comprising the steps of:
a) sorting the photopolymer printing plate materials based on an identifiable property;
b) grinding photopolymer printing plate materials to particles; and
c) screening the particles to remove particles above a certain size to produce the granulated product;
wherein the photopolymer printing plate materials comprise used photocured or photopolymerized flexographic printing elements comprising one or more cured photopolymer layers on a support layer, and wherein the support layer is not removed from the one or more photopolymer layers prior to the grinding step.
2. The method according to claim 1 , wherein the one or more cured photopolymer layers comprise a binder selected from styrene-isoprene-styrene and styrene-butadiene-styrene.
3. The method according to claim 2 , wherein the binder comprises styrene-butadiene-styrene.
4. The method according to claim 1 , wherein the identifiable property is selected from the group consisting of type of binder, Shore A hardness of the photopolymer, printing plate gauge, and combinations of one or more of the foregoing.
5. The method according to claim 1 , wherein the granulated product has a particle size of less than 20 mm.
6. The method according to claim 5 , wherein the granulated product has a particle size of less than 10 mm.
7. The method according to claim 6 , wherein the granulated product has a particle size of less than 5 mm.
8. The method according to claim 1 , wherein an anti-tack agent is added to the granulated product after step c).
9. The method according to claim 1 , wherein the anti-tack agent is selected from the group consisting of fumed silica, tale, mica, clay, carbonate, zinc stearate, magnesium stearate, calcium stearate, potassium stearate, stearic acid, liquid lubricants, emulsified wax, and calcium silicate.
10. An asphalt shingle comprising the granulated product of claim 1 .
11. The asphalt shingle according to claim 10 , wherein the asphalt shingle comprises asphalt and the granulated product, wherein the asphalt shingle comprises about 5% by volume to about 10% by volume of the granulated product.
12. A method of preparing asphalt shingles, the method comprising the step of blending the granulated product of claim 1 with asphalt.
13. The method according to claim 12 , where the step of blending the granulated product with the asphalt comprises mixing the granulated products with the asphalt for a period of about 30 to about 60 minutes at a temperature of between about 350 to about 400° F.