Catalysts and methods for the conversion of carbonaceous materials to liquid fuels
The present disclosure relates to a composition that includes copper (Cu), aluminum (Al), oxygen, and an element (M) that includes at least one of magnesium, cerium, and/or a transition metal, where the copper and the element are present at a first molar ratio relative to the aluminum between about 0.1:1 and about 30:1 ((Cu+M):Al), and the copper and the element are present at a second molar ratio between about 0.1:4 and about 20:1 (Cu:M).
1. A composition comprising:
copper (Cu), aluminum (Al), oxygen, and cerium (Ce); and
an average pore size between about 0.1 nm and about 60 nm, wherein:
the copper and the cerium are present at a first molar ratio relative to the aluminum between about 0.1:1 and about 30:1 ((Cu+Ce):Al),
the copper and the cerium are present at a second molar ratio between about 0.1:4 and about 20:1 (Cu:Ce), and
each of the copper, aluminum, and cerium are covalently incorporated into an oxide.
2. The composition of claim 1 , wherein the second molar ratio is between about 1:1 and about 10:4 (Cu:Ce).
3. The composition of claim 1 , further comprising a third molar ratio of a molar hydrogen (H 2 ) capacity, in moles of H 2 per gram of the composition (c 1 ), to a molar concentration of the Cu, in moles of Cu per gram of the composition (c 2 ), wherein the third molar ratio is between about 0.5:1 and about 10:1 (c 1 :c 2 ).
4. The composition of claim 3 , wherein the third molar ratio is between about 1:1 and about 3.4:1.
5. The composition of claim 1 , wherein the average pore size is between about 1.0 nm and about 10 nm.
6. The composition of claim 1 , further comprising a pore volume between about 0.1 cm 3 /g and about 30 cm 3 /g.
7. The composition of claim 6 , wherein the pore volume is between about 0.1 cm 3 /g and about 1.6 cm 3 /g.
8. The composition of claim 1 , further comprising an acid site density between about 50 μmol acid sites/g composition (μmol/g) and about 350 μmol/g.
9. The composition of claim 8 , wherein the acid site density is between about 125 μmol/g and about 300 μmol/g.
10. The composition of claim 1 , further comprising a surface area between about 50 m 2 /g and about 500 m 2 /g.
11. The composition of claim 10 , wherein the surface area is between about 140 m 2 /g and about 265 m 2 /g.
12. The composition of claim 1 , further comprising a basic site density between about 1.0 μmol basic sites/g composition (μmol/g) and about 200 μmol/g.
13. The composition of claim 12 , wherein the basic site density is between about 25 μmol/g and about 150 μmol/g.
14. A method comprising:
contacting a feedstock comprising at least one of a biomass or a non-biomass carbonaceous material with a composition and supercritical methanol, wherein:
the contacting converts at least a portion of the feedstock to a mixture comprising an alcohol, and
the composition comprises:
copper (Cu), aluminum (Al), oxygen, and cerium (Ce); and
an average pore size between about 0.1 nm and about 60 nm, wherein:
the copper and the cerium are present at a first molar ratio relative to the aluminum between about 0.1:1 and about 30:1 ((Cu+Ce):Al),
the copper and the cerium are present at a second molar ratio between about 0.1:4 and about 20:1 (Cu:Ce), and
each of the copper, aluminum, and cerium are covalently incorporated into an oxide.
15. The method of claim 14 , wherein the contacting is performed at a ratio of the composition to the feedstock between about 1:1 and about 0.01:1.0.
16. The method of claim 14 , wherein the feedstock is solvolyzed in the methanol.
17. The method of claim 14 , wherein the contacting is performed at a temperature between about 200° C. and about 350° C.
18. The method of claim 14 , wherein the contacting is performed at a pressure between about 1200 psig and about 4000 psig.
19. The method of claim 14 , wherein the contacting is performed for a time period between about 2 hours and 8 hours.