Freestanding, dimensionally stable microporous webs
A thin, freestanding, microporous polyolefin web with good heat resistance and dimensional stability includes an inorganic surface layer. A first preferred embodiment is a microporous polyolefin base membrane in which colloidal inorganic particles are present in its bulk structure. Each of second and third preferred embodiments is a thin, freestanding microporous polyolefin web that has an inorganic surface layer containing no organic hydrogen bonding component for the inorganic particles. The inorganic surface layer of the second embodiment is achieved by hydrogen bonding with use of an inorganic acid, and the inorganic surface layer of the third embodiment is achieved by one or both of hydrogen bonding and chemical reaction of the surface groups on the inorganic particles.
1. A freestanding polyolefin web, comprising:
a microporous polyolefin membrane having a first major surface, a second major surface opposite the first major surface, and a bulk structure; and
a porous inorganic surface layer comprising fumed inorganic particles and an inorganic acid, wherein the porous inorganic surface layer covers at least a portion of the first major surface and at least a portion of the second major surface of the polyolefin membrane, wherein the fumed inorganic particles form an aggregated network of open chain shaped morphology, the inorganic particles held together by hydrogen bonding provided by the inorganic acid at particle-to-particle contacts, the inorganic acid comprising at least one of phosphoric acid (H 3 PO 4 ), boric acid (H 3 BO 3 ), tetraboric acid (H 2 B 4 O 7 ), vanadic acid (HVO 3 ), or molybdic acid (H 2 MoO 4 );
wherein the inorganic particles are independently selected from a group consisting of silica, alumina, titania, zirconia, and combinations thereof; and
wherein the polyolefin web exhibits in-plane dimensional stability above the melting point of the polyolefin membrane.
2. The polyolefin web of claim 1 , wherein the porous inorganic surface layer comprises aggregates of inorganic primary particles.
3. The polyolefin web of claim 1 , wherein the porous inorganic surface layer further comprises at least one of colloidal particles or boehmite.
4. The polyolefin web of claim 1 , wherein the fumed inorganic particles have a mean aggregate size of about 100 nm to about 300 nm.
5. The polyolefin web of claim 4 , wherein the fumed inorganic particles have a specific surface area of about 50 m 2 /g to about 225 m 2 /g.
6. The polyolefin web of claim 1 , in which the polyolefin web exhibits pore collapse in the polyolefin membrane and less than 5% shrinkage in either of its in-plane axes at 200° C.
7. The polyolefin web of claim 1 , wherein the porous inorganic surface layer contains an organic hydrogen bonding component.
8. The polyolefin web of claim 7 , wherein the porous inorganic surface layer contains less than or equal to 5 wt. % of the organic hydrogen bonding component.
9. The polyolefin web of claim 1 , wherein the inorganic acid comprises boric acid.
10. The polyolefin web of claim 1 , wherein the inorganic acid comprises phosphoric acid.
11. The polyolefin web of claim 1 , wherein the porous inorganic surface layer consists essentially of the fumed inorganic particles and the inorganic acid.
12. The polyolefin web of claim 1 , wherein the porous inorganic surface layer is free of an organic hydrogen bonding component.
13. The polyolefin web of claim 1 , wherein the porous inorganic surface layer exhibits a pickup weight of 4.14 g/m 2 and a pickup thickness of 3 μm or greater.
14. The polyolefin web of claim 1 , wherein a shrinkage in a machine direction is 2.2 to 5.5 percent and a shrinkage in a transverse direction is 1.2 to 5.3 percent after heating the polyolefin web at 200° C. for 30 minutes.
15. The polyolefin web of claim 1 , wherein the in-plane dimensional stability comprises a shrinkage in a machine direction of the polyolefin web of no more than 11.7 percent and a shrinkage in a transverse direction of the polyolefin web of no more than 9.8 percent after heating the polyolefin web at 200° C. for 30 minutes.
16. A freestanding polyolefin web, comprising:
a microporous polyolefin membrane having a first major surface, a second major surface opposite the first major surface, and a bulk structure; and
a porous inorganic surface layer comprising aggregate inorganic particles and an inorganic acid, wherein the porous inorganic surface layer covers at least a portion of the first major surface and at least a portion of the second major surface of the polyolefin membrane, wherein the aggregate inorganic particles comprise fumed inorganic particles forming an aggregated network of open chain shaped morphology, the inorganic particles held together by hydrogen bonding provided by the inorganic acid at particle-to-particle contacts, the inorganic acid comprising at least one of phosphoric acid (H 3 PO 4 ), boric acid (H 3 BO 3 ), tetraboric acid (H 2 B 4 O 7 ), vanadic acid (HVO 3 ), or molybdic acid (H 2 MoO 4 ); and
wherein the inorganic particles are independently selected from a group consisting of silica, alumina, titania, zirconia, boehmite, and combinations thereof;
wherein the polyolefin web exhibits in-plane dimensional stability above the melting point of the polyolefin membrane, wherein the in-plane dimensional stability comprises a shrinkage in one of a machine direction or a traverse direction of the polyolefin web of no more than about 12 percent after heating the polyolefin web at 200° C. for 30 minutes.
17. The polyolefin web of claim 16 , wherein the in-plane dimensional stability comprises a shrinkage in a machine direction of the polyolefin web of no more than 11.7 percent and a shrinkage in a transverse direction of the polyolefin web of no more than 9.8 percent after heating the polyolefin web at 200° C. for 30 minutes.
18. A method to form a freestanding polyolefin web, the method comprising:
disposing a microporous polyolefin membrane in a dispersion comprising fumed inorganic particles and an inorganic acid to form a porous inorganic surface layer covering at least a portion of a first major surface and at least a portion of a second major surface of the polyolefin membrane to form the polyolefin web, wherein the fumed inorganic particles form an aggregated network of open chain shaped morphology, the inorganic particles held together by hydrogen bonding provided by the inorganic acid at particle-to-particle contacts, the inorganic acid providing thermal stability to the freestanding polyolefin web, the inorganic acid comprising at least one of phosphoric acid (H 3 PO 4 ), boric acid (H 3 BO 3 ), tetraboric acid (H 2 B 4 O 7 ), vanadic acid (HVO 3 ), or molybdic acid (H 2 MoO 4 );
wherein the fumed inorganic particles are independently selected from a group consisting of silica, alumina, titania, zirconia, and combinations thereof; and
wherein the polyolefin web exhibits in-plane dimensional stability above the melting point of the polyolefin membrane.