Cyanide argyrodite solid electrolyte
Disclosed herein are new argyrodite compositions of matter, including, for example, Li 6 PS 5 CN, and methods for making the same.
1. A solid electrolyte comprising Li 6 PS 5 CN wherein the bulk lithium activation barrier for lithium ion conductivity is less than about 242 meV.
2. The solid electrolyte of claim 1 wherein the bulk lithium ion conductivity at 35 degrees Celsius is up to 1.0×10 −5 S/cm.
3. A method for making Li 6 PS 5 CN wherein the Li 6 PS 5 CN exhibits a cubic argyrodite structure comprising a F-43m space group wherein the method comprises the steps of first reacting P 2 S 5 and Li 2 S in THF for a first reaction solution and separately reacting LiCN and Li 2 S in ethanol for a second reaction and then combining the first reaction and the second reaction into the same reaction vessel for a third reaction and wherein the third reaction is dried under vacuum at a temperature of less than 150 degrees Celsius and then isolating the Li 6 PS 5 CN.