Cobalt-chromium alloy resistant to high speed/self-coupled sliding wear
A wrought-able, cobalt-based alloy is disclosed which has extraordinary resistant to high speed/self-coupled sliding wear. This alloy contains about 0.83 wt. % nickel, about 0.125 wt. % nitrogen, about 26.85 wt. % chromium, about 4.58 wt. % molybdenum, about 2.33 wt. % tungsten, about 2.97 wt. % iron, about 0.84 wt. % manganese, about 0.27 wt. % silicon, about 0.065 wt. % carbon, and about 0.11 wt. % aluminum, with the balance cobalt plus impurities.
1. A cobalt-based alloy resistant to high speed/self-coupled sliding wear consisting essentially of 0.83 wt. % nickel, 0.125 wt. % nitrogen, 26.85 wt. % chromium, 4.58 wt. % molybdenum, 2.33 wt. % tungsten, 2.97 wt. % iron, 0.84 wt. % manganese, 0.27 wt. % silicon, 0.065 wt. % carbon, and 0.11 wt. % aluminum, and the balance cobalt plus impurities wherein the alloy has a coefficient of friction between 0.2 and 0.3 at a load of 20N when tested using a pin-on disk method of ASTM Standard G99.
2. The alloy of claim 1 wherein the alloy is in a form selected from the group consisting of plates, sheets, bars, tubes, wires, billets, castings, weldments, weld overlays, and powder products.
3. A cobalt-based alloy resistant to high speed/self-coupled sliding wear consisting essentially of:
0.4546 to 1.2054 wt. % nickel,
0.101 to 0.149 wt. % nitrogen,
25.31 to 28.39 wt. % chromium,
4.04 to 5.12 wt. % molybdenum,
1.79 to 2.87 wt. % tungsten,
1.93 to 4.01 wt. % iron,
0.586 to 1.094 wt. % manganese,
0.03 to 0.51 wt. % silicon,
0.041 to 0.089 wt. % carbon, and
0.0346 to 0.1854 wt. % aluminum, and
the balance cobalt plus impurties;
wherein the alloy has a coefficient of friction between 0.2 and 0.3 at a load of 20N when tested using a pin-on disk method of ASTM Standard G99.
4. The alloy of claim 3 wherein the alloy is in a form selected from the group consisting of plates, sheets, bars, tubes, wires, billets, castings, weldments, weld overlays, and powder products.