A method for depositing a coating comprising a polymer and at least two pharmaceutical agents on a substrate, comprising the following steps: providing a stent framework; depositing on said stent framework a first layer comprising a first pharmaceutical agent; depositing a second layer comprising a second pharmaceutical agent; Wherein said first and second pharmaceutical agents are selected from two different classes of pharmaceutical agents.
1. A method for depositing a coating on a substrate, comprising the steps of:
a. providing a substrate;
b. depositing at least one polymer layer onto said substrate;
c. depositing at least one pharmaceutical layer comprising a pharmaceutical agent onto said substrate without use of a solvent; and
d. sintering said at least one polymer layer so as to produce a polymer film adhered to said substrate under conditions that do not substantially modify a morphology of said pharmaceutical agent,
wherein said pharmaceutical agent comprises a morphology that is crystalline or semi-crystalline.
2. The method of claim 1 , wherein said at least one polymer layers comprises a bioabsorbable polymer.
3. The method of claim 1 , wherein said at least one polymer layer is selected from PLA, PLGA, PGA and Poly(dioxanone).
4. The method of claim 1 comprising depositing 3 or more layers as follows:
a first polymer layer;
the first polymer layer comprising said pharmaceutical agent which is a first pharmaceutical agent;
a second polymer layer;
the second polymer layer comprising a second pharmaceutical agent; and
a third polymer layer.
5. The method of claim 1 comprising depositing 4 or more layers as follows:
a first polymer layer;
a first pharmaceutical layer comprising a first pharmaceutical agent;
a second polymer layer; and
a second pharmaceutical layer comprising a second pharmaceutical agent.
6. The method of claim 1 comprising depositing 4 or more layers as follows:
a first pharmaceutical layer comprising a first pharmaceutical agent;
a first polymer layer;
a second pharmaceutical layer comprising a second pharmaceutical agent; and
a second polymer layer.
7. The method of claim 1 comprising depositing 3 or more layers as follows:
a first pharmaceutical layer comprising a first pharmaceutical agent;
a polymer layer; and
a second pharmaceutical layer comprising a second pharmaceutical agent.
8. The method of claim 1 wherein depositing the at least one polymer layer and depositing the at least one pharmaceutical layer comprises alternating layers of the pharmaceutical layer, or the polymer layer including the pharmaceutical agent, and the polymer layer without the pharmaceutical agent.
9. The method of claim 8 , wherein the pharmaceutical agent layers are substantially free of polymer and the polymer layers are substantially free of pharmaceutical agent.
10. The method of claim 1 , comprising depositing 5, 10, 20, 50, or 100 layers.
11. The method of claim 4 , wherein said first pharmaceutical agent has an elution profile that is slower than the elution profile of the second pharmaceutical agent.
12. The method of claim 11 , wherein the second pharmaceutical agent achieves 100% elution in about 5 days to about 20 days and the first pharmaceutical agent achieves 100% elution in about 120 days to about 180 days.
13. The method of claim 4 , wherein said first pharmaceutical agent is an anti-thrombogenic agent and said second pharmaceutical agent is an anti-restenotic agent.
14. The method of claim 4 , wherein said first pharmaceutical agent is heparin and said second pharmaceutical agent is taxol or a macrolide immunosuppressive drug.
15. The method of claim 2 , wherein said bioabsorbably polymer is selected from PGA poly(glycolide), LPLA poly(l-lactide), DLPLA poly(dl-lactide), PCL poly(e-caprolactone)PDO, poly(dioxolane) PGA-TMC, 85/15 DLPLG p(dl-lacide-co-glycolide), 75/25 DLPLG, 65/35 DLPLG, 50/50 DLPLG, TMC poly(trimetylcarbonate), p(CPP:SA) poly(1,3-bis-p-(carboxyphenoxy)propane-co-sebacic acid).
16. The method of claim 1 , wherein at least one of said pharmaceutical agents comprises a macrolide immunosuppressive drug.
17. The method of claim 16 , wherein said macrolide immunosuppressive drug is at least 50% crystalline.
18. The method of claim 1 , wherein said depositing at least one polymer layer comprises depositing polymer particles on said substrate by an RESS process.
19. The method of claim 1 , wherein the at least one polymer layer is deposited in dry powder form.
20. The method of claim 1 , wherein the at least one pharmaceutical layer is deposited in dry powder form.