Hot rolled coated steel sheet having high strength, high formability, excellent bake hardenability and method of manufacturing same
A hot-rolled coated steel sheet including: in wt %, C: 0.05-0.14%, Si: 0.1-1.0%, Mn: 1.0-2.0%, P: 0.001-0.05%, S: 0.001-0.01%, AI: 0.01-0.1%, Cr: 0.005-1.0%, Ti: 0.005-0.13%, Nb: 0.005-0.03%, N: 0.001-0.01%, Fe residues, and other inevitable impurities; a mixed structure of ferrite and bainite as a main phase; and as a remaining structure, one or more selected from the group consisting of martensite, austenite, and phase martensite (MA), wherein a fraction of the ferrite and bainite is 95-99 area % and Equation 1 is satisfied. [Equation 1] FCO {110}<112> +FCO {112}<111> ≥10 where, FCO {110}<112> and FCO {112}<111> , each representing an area fraction occupied by a structure having ac crystal orientation of {110}<112> and {112}<111>.
1. A hot-rolled coated steel sheet comprising: in wt %,
C: 0.05-0.14%, Si: 0.1-1.0%, Mn: 1.0-2.0%, P: 0.001-0.05%, S: 0.001-0.01%, Al: 0.01-0.1%, Cr: 0.005-1.0%, Ti: 0.005-0.13%, Nb: 0.005-0.03%, N: 0.001-0.01%, and a balance of Fe and inevitable impurities,
wherein the hot-rolled coated steel sheet comprises a mixed structure of ferrite and bainite as a main phase, and as a remaining structure, one or more selected from a group consisting of martensite, austenite, and phase martensite (MA),
wherein a fraction of the ferrite and bainite is 95 to 99 area%, and Equation 1 is satisfied,
FCO {110}<112> +FCO {112}<111> ≥10 [Equation 1]
where, FCO {110}<112> and FCO {112}<111> , each represents an area fraction occupied by a structure having ac crystal orientation of { 110 }< 112 > and { 112 }< 111 >.
2. The hot-rolled coated steel sheet of claim 1 , wherein a fraction of bainite is 3 to 30 area%.
3. The hot-rolled coated steel sheet of claim 1 , wherein the hot-rolled coated steel sheet has bake hardenability (BH): 30 MPa or more, tensile strength (TS): 780 MPa or more, an elongation rate (El): 10% or more, a yield ratio (YR): 0.8 or more, and stretch-flangeability: 40% or more.
4. The hot-rolled coated steel sheet of claim 1 , wherein in the hot-rolled coated steel sheet, a plating layer including one or more of zinc or aluminum is formed on one side or both sides of a base steel sheet.