BLOWING AGENT BLENDS
This invention relates to the use of HFO-1336mzz-Z blends as blowing agents for thermoplastic polymers (e.g., polystyrene).
1 . A process for preparing a thermoplastic polymer foam, the process comprising:
(a) providing a foamable composition comprising a thermoplastic polymer and a blowing agent, wherein the blowing agent comprises from about 95% to about 1% by weight Z-1,1,1,4,4,4-hexafluoro-2-butene and from about 1% to about 95% by weight 2-chloropropane; and
(b) expanding the foamable composition to produce the thermoplastic polymer foam.
2 . The process of claim 1 , wherein the solubility of the blowing agent in the polymer is greater than the solubility of the Z-1,1,1,4,4,4-hexafluoro-2-butene, alone, in the polymer.
3 . The process of claim 1 , wherein the blowing agent comprises about 50% to about 10% by weight Z-1,1,1,4,4,4-hexafluoro-2-butene.
4 . The process of claim 1 , wherein the blowing agent comprises about 1% to about 30% by weight 2-chloropropane.
5 . The process of claim 1 , wherein the blowing agent comprises up to about 80% by weight Z-1,1,1,4,4,4-hexafluoro-2-butene and at least about 20% by weight 2-chloropropane.
6 . The process of claim 1 , wherein the blowing agent consists essentially of Z-1,1,1,4,4,4-hexafluoro-2-butene and 2-chloropropane.
7 . The process of claim 1 , wherein the blowing agent further comprises HFC-152a.
8 . The process of claim 7 , wherein the solubility of the blowing agent in the polymer is greater than the solubility of the Z-1,1,1,4,4,4-hexafluoro-2-butene, alone, in the polymer.
9 . The process of claim 7 , wherein the blowing agent comprises about 5% to about 60% by weight Z-1,1,1,4,4,4-hexafluoro-2-butene.
10 . The process of claim 7 , wherein the blowing agent comprises about 1% to about 20% by weight 2-chloropropane.
11 . The process of claim 7 , wherein the blowing agent comprises about 5% to about 95% by weight HFC-152a.
12 . The process of claim 7 , wherein the blowing agent consists essentially of Z-1,1,1,4,4,4-hexafluoro-2-butene, 2-chloropropane, and HFC-152a.
13 . The process of claim 1 , wherein the thermoplastic polymer is selected from the group consisting of polystyrene, polyethylene, polyethylene copolymer, polypropylene, polypropylene copolymer, acrylonitrile butadiene styrene, and styrene acrylonitrile copolymer, and blends thereof.
14 . The process of claim 1 , wherein the thermoplastic polymer is selected from the group consisting of a polystyrene homopolymer, a polystyrene copolymer, styrene-acrylonitrile copolymer, and blends thereof.
15 . The process of claim 1 , wherein the process is performed at a pressure just before foaming of from about 100 psi to about 5000 psi.
16 . The process of claim 1 , further comprising extruding the thermoplastic polymer to form the thermoplastic polymer foam.
17 . The process of claim 16 , wherein the extruding is performed at a die temperature of from about 100° C. to about 150° C.
18 . The process of claim 1 , wherein the polymer foam is a closed cell polymer foam.
19 . The process of claim 18 , wherein the polymer foam is a smooth skin polymer foam.
20 . The process of claim 18 , wherein the polymer foam is substantially free of blowholes.
21 . The process of claim 1 , wherein the polymer is a polystyrene homopolymer.
22 . The process of claim 1 wherein the foamable composition further comprises nucleating agent.
23 . The process of claim 22 , wherein the nucleating agent is selected from the group consisting of talc, graphite, and magnesium silicate.
24 . The process of claim 1 , wherein the foamable composition further comprises a flame retardant.
25 . The process of claim 24 , wherein the flame retardant comprises a polymeric flame retardant or a halogenated flame retardant.
26 . The process of claim 24 , wherein the flame retardant is a brominated flame retardant or a chlorinated flame retardant.
27 . The process of claim 24 , wherein the flame retardant is PolyFR.
28 . The process of claim 1 , wherein the foamable composition further comprises an Infrared Attenuating Agent.
29 . The process of claim 1 , wherein the blowing agent is from about 1 part to about 25 parts per hundred parts of polymer by mass.
30 . The process of claim 1 , wherein the blowing agent is from about 7 parts to about 18 parts per hundred parts of polymer by mass.
31 . A thermoplastic polymer foam, comprising:
(a) a thermoplastic polymer selected from the group consisting of polystyrene homopolymer, a polystyrene copolymer, and styrene-acrylonitrile copolymer, or a blend thereof; and
(b) a blowing agent comprising from 95% to 1% by weight Z-1,1,1,4,4,4-hexafluoro-2-butene and from 1% to 95% by weight 2-chloropropane.
32 . The thermoplastic polymer foam of claim 31 , wherein the blowing agent further comprises HFC-152a.