Main agent uniformly dispersed microsphere and a sustained release formulation comprising the same
The present application provides a microsphere in which a main agent is uniformly dispersed in a polymer matrix, wherein an average volume-based particle diameter of the microsphere is 1 μm or more and 150 μm or less, and a variation coefficient of area ratios in four regions is 0.35 or less, wherein the area ratios in four regions are calculated by (s/A)×100(%) wherein the four regions are prepared by preparing a cross section observation sample obtained by cutting the microsphere; observing the cross section observation sample with an electron microscope at a magnification capable of confirming the main agent in the microsphere or a higher magnification; and dividing the electron microscope observation image into four regions; and A is an area of a respective divided region, and s is a sum of cross section areas of the main agent included in the respective divided region. The microsphere of the present invention can appropriately control the initial release amount of the main agent and its release rate during a subsequent release period, and can continuously release the main agent for a predetermined period of time.
1. A microsphere in which a main agent is uniformly dispersed in a polymer matrix,
wherein an average volume-based particle diameter of the microsphere is 1 μm or more and 150 μm or less, and
a variation coefficient of area ratios in four regions is 0.25 or less, wherein the area ratios in four regions are calculated by (s/A)×100 (%) wherein the four regions are prepared by preparing a cross section observation sample obtained by cutting the microsphere; observing the cross section observation sample with an electron microscope at a magnification capable of confirming the main agent in the microsphere or a higher magnification; and dividing the electron microscope observation image into four regions; and A is an area of a respective divided region, and s is a sum of cross section areas of the main agent included in the respective divided region,
the polymer matrix is composed of at least one polymer selected from the group consisting of poly (lactide-co-glycolide) (PLGA), polylactide (PLA), polycaprolactone (PCL) and ethyl cellulose (EC),
the main agent is a pharmaceutical compound, a functional food compound, a functional cosmetic compound, an animal administration compound, or an agricultural compound, which is lipophilic,
a content of the main agent in the microsphere is 0.10 to 50% by mass relative to the total amount of the microsphere, and
the microsphere is produced by continuously feeding to a pulverizing apparatus a solution containing the at least one polymer and the main agent obtained by dissolving or dispersing the at least one polymer and the main agent in a good solvent of the at least one polymer with high speed stirring, and a solution containing a poor solvent of the at least one polymer to prepare emulsified particles; and removing the good solvent from the produced particles,
a content of the at least one polymer is 1 to 30% by mass relative to the total mass of the solution containing the at least one polymer and the main agent, and
the removal of the good solvent is performed by flowing a gas, or by using an evaporator under a reduced pressure.
2. The microsphere according to claim 1 , wherein an average particle diameter of the dispersed main agent is 5 nm to 500 nm.
3. A sustained release formulation comprising the microsphere according to claim 1 .
4. A sustained release formulation comprising the microsphere according to claim 2 .