Blends for foams, foams manufactured therefrom and articles comprising the same
Disclosed herein is a foamable composition comprising an olefin copolymer that comprises ethylene and an α-olefin; an unneutralized carboxylated olefin copolymer; a crosslinking agent; a blowing agent; and an activator; where a weight ratio of the activator to the unneutralized carboxylated olefin copolymer is greater than 0.3. Disclosed herein too is a method of manufacturing a foamable composition comprising blending together an olefin copolymer that comprises ethylene and an α-olefin; an unneutralized carboxylated olefin copolymer; a crosslinking agent; a blowing agent; and an activator to form the foamable composition; where a weight ratio of the activator to the unneutralized carboxylated olefin copolymer is greater than 0.3; heating the foamable composition to activate the blowing agent to form a foam; and crosslinking the foam.
1. A foam produced from a foamable composition comprising:
an olefin copolymer that comprises ethylene and an α-olefin;
an unneutralized carboxylated olefin copolymer comprising a carboxylic acid;
a crosslinking agent;
a blowing agent; and
an activator that comprises a metal oxide, a metal hydroxide, a metal salt, or a combination thereof,
wherein:
a weight ratio of the activator to the unneutralized carboxylated olefin copolymer is greater than 0.51;
the unneutralized carboxylated olefin copolymer has a melt index (measured at 2.16 kg and 190° C. as per ASTM D1238) of less than or equal to 5 g/10 min and is present in the foamable composition in an amount of 5 wt % to 20 wt %, based on a total weight of the resin in the foamable composition; and
neutralized carboxylated olefin copolymer is formed during foam production.
2. The foam of claim 1 , wherein the olefin copolymer is an olefin block copolymer and is present in the foamable composition in an amount of 60 wt % to 90 wt %, based on the total weight of the foamable composition.
3. The foam of claim 1 , wherein the α-olefin is 1-octene.
4. The foam of claim 1 , wherein the unneutralized carboxylated olefin copolymer is present in the foamable composition in an amount 5 wt % to 10 wt %, based on a total weight of the resin in the foamable composition.
5. The foam of claim 1 , wherein the carboxylic acid is acrylic acid or methacrylic acid.
6. The foamable composition of claim 1 , wherein the crosslinking agent is a peroxide, and wherein the blowing agent is an azodicarbonamide.
7. The foam of claim 1 , wherein the foam has a density of 0.15 g/cc to 0.20 g/cc, an Asker C hardness of 40 to 60 when measured as per ASTM D2240, and a split tear of greater than 2.4 N/mm when measured as per ASTM D3574.
8. An article manufactured from the foam of claim 1 .
9. The article of claim 8 , wherein the article is a footwear shoe sole.
10. A method of manufacturing a crosslinked foam, the method comprising:
blending together an olefin copolymer that comprises ethylene and α-olefin, an unneutralized carboxylated olefin crosslinking agent, a blowing agent, and an activator to form a foamable composition, wherein:
a weight ratio of the activator to the unneutralized carboxylated olefin copolymer is greater than 0.51; and
the unneutralized carboxylated olefin has a melt index (measured at 2.16 kg and 190° C. as per ASTM D1238) of less than or equal to 5 g/10 min; and
heating the foamable composition to activate the blowing agent and crosslinked agent to form the crosslinked foam, wherein the crosslinked foam comprises neutralized carboxylated olefin copolymer.
11. The method of claim 10 , further comprising molding the foam.
12. A foam produced from a foamable composition comprising:
an olefin copolymer that comprises ethylene and an α-olefin;
an unneutralized carboxylated olefin copolymer comprising a carboxylic acid;
a crosslinking agent;
a blowing agent; and
an activator that comprises a metal oxide, a metal hydroxide, a metal salt, or a combination thereof,
wherein:
a weight ratio of the activator to the unneutralized carboxylated olefin copolymer is greater than or equal to 0.6; and
the unneutralized carboxylated olefin copolymer is present in the foamable composition in an amount of 5 wt % to 20 wt %, based on a total weight of the resin in the foamable composition.