Methods for producing metal matrix composite strip product
Methods for producing a coiled strip of metal matrix composite (MMC) material are disclosed. The methods include a combination of hot rolling and warm rolling processes that reduce the thickness of the input material and increase its ductility. The resulting MMC strip can be coiled, which is useful for high volume coil-to-coil applications.
1. A method for producing a strip of a metal matrix composite (MMC) material, comprising:
hot working a rectangular input of the MMC material to produce a hot rolled MMC material; and
warm working the hot rolled MMC material to obtain the strip of MMC material, wherein the warm working is performed using heated rolls.
2. The method of claim 1 , further comprising winding the strip of MMC material into a coil.
3. The method of claim 1 , wherein the hot working is performed at a temperature from about 900° F. (482° C.) to about 1050° F. (565° C.).
4. The method of claim 1 , wherein the hot working is performed to a total % HW of at least 75%.
5. The method of claim 1 , wherein the hot working is performed by a plurality of hot passes, each hot pass resulting in a % HW of up to 20%.
6. The method of claim 1 , wherein the warm working is performed at a temperature from about 350° F. to about 600° F. (about 177° C. to about 315° C.).
7. The method of claim 1 , wherein the warm working is performed to a total % WW of at least 75%.
8. The method of claim 1 , wherein the warm working is performed by a plurality of warm passes, each warm pass resulting in a % WW of up to 65%.
9. The method of claim 1 , further comprising cold working the strip of MMC material after the warm working.
10. The method of claim 9 , wherein the cold working is performed to a total % CW of about 10% or less.
11. The method of claim 1 , wherein the MMC material comprises an aluminum alloy and ceramic particles dispersed in the aluminum alloy.
12. The method of claim 11 , wherein the ceramic particles comprise at least one ceramic material selected from the group consisting of carbides, oxides, silicides, borides, and nitrides.
13. The method of claim 1 , wherein the MMC material comprises from about 15 vol % to about 50 vol % of the ceramic particles.
14. The method of claim 1 , wherein the average particle size of the ceramic particles is from about 0.3 μm to about 0.5 μm.