Ferrite-based stainless steel having excellent processability and high-temperature strength and method for manufacturing same
Disclosed is a ferritic stainless steel with improved workability and high temperature strength through control of component composition and precipitate distribution, and a manufacturing method thereof. The ferritic stainless steel excellent in workability and high temperature strength according to an embodiment of the present disclosure includes, in percent (%) by weight of the entire composition, C: 0.0005 to 0.02%, N: 0.005 to 0.02%, Si: 0.01 to 1.0%, Mn: 0.01 to 1.2%, P: 0.001 to 0.05%, Cr: 10.0 to 25.0%, Mo: 1.5 to 3.0%, Nb: 0.3 to 0.7%, W: 0.5 to 2.0%, the remainder of iron (Fe) and other inevitable impurities, and the number of precipitates with an average diameter of 0.5 μm or less is 10 5 pieces/mm 2 or less.
1. A ferritic stainless steel comprising, in percent (%) by weight of the entire composition, C: 0.0005 to 0.02%, N: 0.005 to 0.02%, Si: 0.01 to 1.0%, Mn: 0.01 to 1.2%, P: 0.001 to 0.05%, Cr: 10.0 to 25.0%, Mo: 1.5 to 3.0%, Nb: 0.3 to 0.7%, W: 0.5 to 2.0%, and the remainder of iron (Fe),
wherein the ferritic stainless steel includes precipitates including a Laves phase precipitate comprising a Laves phase,
wherein the Laves phase precipitate comprises Mo Laves phase precipitate, Nb Laves phase precipitate, and W Laves phase precipitate,
wherein a number of precipitates with an average diameter of 0.5 μm or less is 10 5 pieces/mm 2 or less, and
wherein a weight ratio of W to a total weight of the Laves phase precipitate is less than 20%.
2. The ferritic stainless steel of claim 1 , wherein the stainless steel has an elongation of 27% or more at 25° C., and a tensile strength of 45 MPa or more at 900° C.
3. The ferritic stainless steel of claim 1 , comprising, in percent (%) by weight of the entire composition, Mn: 0.01 to 0.5%.