Polyamide foam preparation
Disclosed herein is a foamed composition comprising 55 to 98 wt. % of polyamide, and 2 to 45 wt. % of ionomer comprising a zinc neutralized ethylene acid copolymer. The zinc neutralized ethylene acid copolymer is the polymerized reaction product of ethylene monomer, monocarboxylic acid monomer, and unsaturated dicarboxylic acid monomer, and 30 to 70 mole percent of total acid units of the ionomer are neutralized.
1. A foam comprising:
55 to 98 wt. % polyamide; and
2 to 45 wt. % of ionomer consisting of a zinc neutralized ethylene acid copolymer,
wherein the zinc neutralized ethylene acid copolymer is the polymerized reaction product of ethylene monomer, monocarboxylic acid monomer, and unsaturated dicarboxylic acid monomer, and
wherein 30 to 70 mole percent of total acid units of the ionomer are neutralized;
wherein a foam structure of the foam is formed by a pressure drop from 15 to 30 MPa/sec, within a second.
2. The foam of claim 1 , wherein the foam has a density of 0.03 to 0.5 g/cc.
3. The foam of claim 1 , wherein the foam has an expansion ratio of at least 1500%.
4. The foam of claim 1 , wherein the foam is free of polyurethane.
5. The foam of claim 1 , wherein the foam comprises 75 to 97 wt. % polyamide.
6. The foam of claim 1 , wherein the polyamide comprises aliphatic polyamide.
7. The foam of claim 1 , wherein the polyamide comprise PA 6, PA 11, PA 12, or combinations thereof.
8. The foam of claim 1 , wherein the foam comprises 3 to 20 wt. % ionomer.
9. The foam of claim 1 , wherein the zinc neutralized ethylene acid copolymer comprises at least 50% ethylene monomer, based on the total wt. % of the monomers present in the zinc neutralized ethylene acid copolymer.
10. The foam of claim 1 , wherein the zinc neutralized ethylene acid copolymer comprises at least 5 to 25 wt. % of monocarboxylic acid monomer, based on the total wt. % of the monomers present in the zinc neutralized ethylene acid copolymer.
11. The foam of claim 1 , wherein the zinc neutralized ethylene acid copolymer comprises 2 to 20 wt. % of unsaturated dicarboxylic acid monomer, based on the total wt. % of the monomers present in the zinc neutralized ethylene acid copolymer.
12. The foam of claim 1 , wherein the unsaturated dicarboxylic acid monomer comprises maleic anhydride, maleic anhydride mono-methyl ester, maleic anhydride mono-ethyl ester, maleic anhydride mono-propyl ester, maleic anhydride mono-butyl ester, or combinations thereof.
13. The foam of claim 1 , wherein the monocarboxylic acid monomer comprises methacrylic acid, acrylic acid, or combinations thereof.
14. A method of producing foam comprising:
injecting supercritical blowing agent of CO 2 , N 2 or a combination of both into a vessel to mix with a foam precursor mixture, wherein the vessel is at a pressure and temperature above the supercritical temperature and pressure of the blowing agent, and wherein the foam precursor mixture comprises 55 to 98 wt. % polyamide; and 2 to 45 wt. % of ionomer consisting of a zinc neutralized ethylene acid copolymer,
wherein the zinc neutralized ethylene acid copolymer is the polymerized reaction product of ethylene monomer, monocarboxylic acid monomer, and unsaturated dicarboxylic acid monomer, and
wherein 30 to 70 mole percent of total acid units of the ionomer are neutralized;
producing the foam by dropping the pressure below the pressure of the supercritical blowing agent at a pressure drop from 15 to 30 MPa/sec within a second.
15. The foam of claim 1 , wherein
the foam has a density of 0.03 to 0.5 g/cc, and
the foam has an expansion ratio of at least 1500%.
16. The foam of claim 15 , wherein the foam is free of polyurethane.
17. The foam of claim 16 , wherein the foam comprises 75 to 97 wt. % polyamide.
18. The foam of claim 1 , wherein the foam comprises a foam composition comprising a melt shear viscosity (v 100 ) of greater than 500 Pa*s at a shear rate of 100 radians/second and at a temperature of 270° C.
19. The foam of claim 1 , wherein the monocarboxylic acid monomer is maleic anhydride mono-methyl ester.