Upgraded recycled relatively polyethylene rich polyolefin materials

1. A polyethylene-polypropylene composition obtainable by blending:

a) 80 to 97 wt. % of a blend (A) comprising

A-1) polypropylene and

A-2) polyethylene,

wherein the weight ratio of polypropylene to polyethylene is from 3:7 to 13:7, and

wherein blend (A) is a recycled material, which is recovered from a waste plastic material derived from post-consumer and/or post-industrial waste; and whereby blend (A) has a content of limonene as determined by using solid phase microextraction (HS-SPME-GC-MS) of from 1 ppm to 100 ppm, and

b) 3 to 20 wt. % of a compatibilizer (B) being a heterophasic random copolymer comprising a random polypropylene copolymer matrix phase and an elastomer phase dispersed therein, whereby;

the heterophasic random copolymer has:

a xylene insoluble content (XCI) of from 65 to 88 wt. % (ISO 16152, 1 ed, 25° C.), and

a xylene soluble content XCS of 12 to 35 wt. % (ISO 16152, 1 ed, 25° C.), the XCS fraction having an intrinsic viscosity (measured in decalin according to DIN ISO 1628/1 at 135° C.) of 1.2 dl/g to less than 3.0 dl/g, and

a flexural modulus of from 300 to 600 MPa (ISO 178, measured on injection moulded specimens, 23° C.);

wherein the ratio of MFR 2 (blend (A))/MFR 2 (compatibilizer(B)) ((ISO1133, 2.16 kg load at 230° C.), is in the range 0.5 to 1.5; and

wherein xylene insoluble content (XCI) and xylene soluble content (XCS) add up to 100 wt. %, and wherein the polyethylene-polypropylene composition has a tensile modulus of at least 800 MPa (measured according to ISO 527-2) using injection moulded specimens as described in EN ISO 1873-2 (dog bone shape, 4 mm thickness)).

2. The polyethylene-polypropylene composition according to claim 1 , whereby the compatibilizer (B) has a tensile strain at break (MD) of at least 500%.

3. The polyethylene-polypropylene composition according to claim 1 , whereby the compatibilizer (B) has a content of units derived from ethylene in the xylene insoluble (XCI) fraction of from 2.0 to 6.0 wt. % and/or whereby the compatibilizer (B) has a content of units derived from ethylene in the xylene soluble (XCS) fraction of 25.0 to 38.0 wt. %.

4. The polyethylene-polypropylene composition according to claim 1 , whereby the compatibilizer (B) has an MFR 2 (IS01133; 2.16 kg; 230° C.) of 5 to 15 g/10 min and/or whereby the compatibilizer (B) has a total content of units derived from ethylene of 5.0 to 10.0 wt. %.

5. The polyethylene-polypropylene composition according to claim 1 , whereby the xylene soluble (XCS) fraction of compatibilizer (B) has an intrinsic viscosity (measured in decalin according to DIN ISO 1628/1 at 135° C.) of 1.3 to less than 2.2 dl/g.

6. The polyethylene-polypropylene composition according to claim 1 , whereby the compatibilizer (B) has a flexural modulus of 400 to 550 MPa (ISO 178, measured on injection-moulded specimens, 23° C.).

7. The polyethylene-polypropylene composition according to claim 1 , whereby blend (A) has a content of limonene as determined by using solid phase microextraction (HS-SPME-GC-MS) of from 1 ppm to 100 ppm.

8. The polyethylene-polypropylene composition according claim 1 , having a Charpy notched impact strength (1eA) (non-instrumented, ISO 179-1 at +23° C.) of at least 6.0 kJ/m 2 and/or having Charpy notched impact strength (1eA) (non-instrumented, ISO 179-1 at −30° C.) of at least 2.5 kJ/m 2 and/or a tensile strain at break (ISO 527-1,2) of at least 75%.

9. The polyethylene-polypropylene composition according to claim 1 , whereby blend (A):

(i) contains less than 6.0 wt. % polystyrene; and/or

(ii) contains less than 3 wt. % talc; and/or

(iii) contains less than 5.0 wt. % polyamide and/or

(iv) contains less than 3 wt. % chalk.

10. A process for the manufacture of a polyethylene-polypropylene composition according to claim 1 , wherein the process comprises the steps of:

a) providing blend (A) comprising polypropylene and polyethylene in a ratio of 3:7 to 13:7 in amount of at least 80 wt. %, based on the total weight of the polyethylene-polypropylene composition, whereby blend (A) has a content of limonene as determined by using solid phase microextraction (HS-SPME-GC-MS) of from 1 ppm to 100 ppm,

b) providing a compatibilizer (B) being a heterophasic random copolymer comprising a random polypropylene copolymer matrix phase and an elastomer phase dispersed therein in an amount from 3 to 20 wt. %, based on the total weight of the polyolefin composition, wherein

the heterophasic random copolymer has:

xylene insoluble content (XCI) of 65 to 88 wt. % (ISO 16152, 1 ed, 25° C.), and

a xylene soluble content (XCS) of 12 to 35 wt. % (ISO 16152, 1 ed, 25° C.), the XCS having an intrinsic viscosity IV(XCS) (measured in decalin according to DIN ISO 1628/1 at 135° C.) of 1.2 dl/g to less than 3.0 dl/g, and

the ratio of MFR 2 (blend (A))/MFR 2 (compatibilizer(B)) (IS01133, 2.16 kg load at 230° C.), is in the range 0.5 to 1.5, and

c) melting and mixing the blend of blend (A) and the compatibilizer (B)

d) optionally cooling down said mixture compound and pelletizing.

11. An article comprising the composition according to claim 1 , for use in a consumer application.