Non-grain oriented electrical steel and method for manufacturing same
A non-oriented electrical steel sheet according to an embodiment of the present invention includes: in wt %, C at 0.004 wt % or less (excluding 0 wt %), Si at 2.5 to 4.0 wt %, P at 0.1 wt % or less (excluding 0 wt %), Al at 0.3 to 2.0 wt %, N at 0.003 wt % or less (excluding 0 wt %), S at 0.003 wt % or less (excluding 0 wt %), Mn at 0.15 to 2.5 wt %, Cr at 0.5 wt % (excluding 0 wt %), and the balance including Fe and other impurities unavoidably added thereto; satisfies the following Equation 1; and has an average grain size of 20 μm or less. [Mn]≥1450×[S]−0.8 [Equation 1] (In Equation 1, [Mn] and [S] represent a content (wt %) of Mn and S, respectively.).
1. A non-oriented electrical steel sheet, comprising:
in wt %, C at 0.004 wt % or less and greater than 0 wt %, Si at 2.5 to 4.0 wt %, P at 0.1 wt % or less and greater than 0 wt %, Al at 0.3 to 2.0 wt %, N at 0.003 wt % or less and greater than 0 wt %, S at 0.003 wt % or less and greater than 0 wt %, Mn at 0.15 to 2.5 wt %, Cr at 0.001 wt % to 0.2 wt %, Cu at 0.1 wt % or less and the balance including Fe and other impurities unavoidably added thereto;
satisfying Equation 1 below; and
having an average grain size of 20 μm or less:
[Mn]≥1450×[S]−0.8 [Equation 1]
wherein in Equation 1, [Mn] and [S] represent a content in wt % of Mn and S, respectively,
wherein a density of sulfide having a diameter of 1 nm to 0.1 μm is 10,000/mm 2 to 240,000/mm 2 .
2. The non-oriented electrical steel sheet of claim 1 , further comprising
one or more of Ti at 0.003 wt % or less, and Nb at 0.003 wt % or less.
3. The non-oriented electrical steel sheet of claim 1 , wherein the sulfide includes MnS or CuS.
4. The non-oriented electrical steel sheet of claim 1 , wherein
a magnetic flux density (B 50 ) induced in a magnetic field of 5000 is 1.61 T or more, and the non-oriented electrical steel sheet has a yield strength of 500 MPa or more.
5. The non-oriented electrical steel sheet of claim 1 , wherein
iron loss (W 10/400 ) measured after stress relief annealing that is performed at a temperature of 750° C. for 2 hours is 12 W/kg or less.