Transparent polymeric composition
A polyamide-based polymer composition including: a) 50% to 98% by weight of a transparent amorphous polyamide; b) 1% to 15% by weight of a polymer in the form of core-shell particles; and c) 1% to 15% by weight of a polyether block and polyamide block copolymer, wherein the polyether block and polyamide block copolymer has: as a 2 mm layer, a transmittance at 560 nm of 90% or more; and a refractive index that does not differ by more than 0.01 from that of the transparent amorphous polyamide and wherein the polymer in the form of core-shell particles has a refractive index that does not differ by more than 0.01 from that of the transparent amorphous polyamide. Also, a process for the manufacture of the composition, and the composition capable of being obtained by said process.
1. A polyamide-based polymer composition comprising:
a) 50% to 98% by weight of polyamide consisting of transparent amorphous polyamide;
b) 1% to 15% by weight of a polymer in the form of core-shell particles; and
c) 1% to 15% by weight of a polyether block and polyamide block copolymer,
wherein said polyether block and polyamide block copolymer has:
as a 2 mm layer, a transmittance at 560 nm of 90% or more and
a refractive index that does not differ by more than 0.01 from that of the transparent amorphous polyamide,
and wherein the polymer in the form of core-shell particles has a refractive index that does not differ by more than 0.01 from that of the transparent amorphous polyamide.
2. The polymer composition as claimed in claim 1 , wherein the polymer in the form of core-shell particles comprises no more than 10 mol % of aromatic monomers.
3. The polymer composition as claimed in claim 1 , wherein the transparent amorphous polyamide is chosen from TMDT, TMDI, TMD18, TMD14, TMD12, TMD10, MPMDT, MPMDI, MPMD18, MPMD14, MPMD12, MPDM10, B10, B11, B12, B13, B14, B16, B18, B19, B20, B21, BI, P10, P11, P12, P13, P14, P16, P18, P19, P20, PI, P21, 11/BI, 11/BT, 12/BI, 12/BT, 11/B10, 12/B10, 11/P10, 12/P10, 11/B12, 12/B12, 11/P12, 12/P12, 11/B14, 12/B14, 11/P14, 12/P14, 11/B18, 12/B18, 11/P18, 12/P18, 6.10/BI, 6.10/BT, 10.10/BI, 10.10/BT, 6.12/BI, 612/BI, 1012/BI, 1012/BT, 610/PI, 610/PT, 1010/PI, 1010/PT, 612/PI, 612/PT, 1012/PI, 1012/PT, 610/B10, 610/B12, 610/B14, 610/B18, 1010/B10, 1010/B12, 1010/B14, 1010/B18, 1012/B10, 1012/B12, 1012/B14, 1012/B18, 610/P10, 610/P12, 610/P14, 610/P18, 1010/P10, 1010/P12, 1010/P14, 1010/P18, 1012/P10, 1012/P12, 1012/P14, 1012/P18, B10/P10, B12/P12, B14/P14 12/B I/BT, 11/BI/BT, 12/PI/PT, 11/P I/PT, 11/B10/BT, 11/B12/BT, 11/P10/PT, 12/B10/BI, 12/B12/BI, 12/P10/PI, 12/P12/PI, 12/B10/BT, 12/B12/BT, 12/P10/PT, 12/P12/PT, 11/B10/BI, 11/B12/BI, 11/P10/PI, 11/P12/PI, 11/P12/PT, 11/B10/B14, 11/P10/P14, 11/B12/B14, 11/P12/P14, 12/B10/B14, 12/P10/P14, 12/B12/B.4, 12/P12/P14, 11/B10/B12, 11/P10/P12, 12/B10/B12, 12/P10/P12, 11/P12/B12, 12/P12/B12, 11/P10/B10, 12/P10/B10, 12/BI, 12/BT, B12, 11/B14 and 11/B10 polyamides.
4. The polymer composition as claimed in claim 1 , wherein the transparent amorphous polyamide is PA 11/B10.
5. The polymer composition as claimed in claim 4 , wherein the molar ratio of the number of moles of aminoundecanoic acid to the number of moles of diamine forming the polyamide in the transparent amorphous polyamide is between 0.01 and 0.5.
6. The polymer composition as claimed claim 1 , wherein the polymer in the form of core-shell particles comprises a layer (A) comprising a polymer (A1) having a glass transition temperature Tg A1 below 0° C. and a layer (B) comprising a polymer (B1) having a glass transition temperature Tg B1 above 60° C.
7. The polymer composition as claimed in claim 6 , wherein the polymer (B1) is a (meth)acrylic polymer.
8. The polymer composition as claimed in claim 6 , wherein the polymer (B1) comprises at least 80% by weight of C1 to C4 alkyl methacrylate monomers and/or of C1 to C8 alkyl acrylate monomers.
9. A process for manufacturing a polyamide-based polymer composition as defined in claim 1 , comprising the step of mixing
a) 50% to 98% by weight of a transparent amorphous polyamide;
b) 1% to 15% by weight of a polymer in the form of core-shell particles; and
c) 1% to 15% by weight of a polyether and polyamide block copolymer,
wherein said polyether and polyamide block copolymer has:
as a 2 mm layer, a transmittance at 560 nm of 90% or more and
a refractive index that differs by 0.01 or less from that of the transparent amorphous polyamide, and
wherein the polymer in the form of core-shell particles has a refractive index that does not differ by more than 0.01 from that of the transparent amorphous polyamide.
10. The polymer composition obtained by the process as claimed in claim 9 .
11. An article comprising a composition as claimed in claim 1 in at least one part or one layer.
12. The article as claimed in claim 11 , wherein the article is a molded object, a sheet, a profiled element, a tube, a hollow body or an optically variable filter or an optical lens, optical recording systems, flowmeters, rupture disks, screens, optical data storage, housings or parts of housings, a decorative element or a structural element, a part of a sports shoe, or golf equipment, or a cover, a part of electronic equipment, storage media, infrared keys, portable recording devices, personal digital assistants, smartphones, a coating, sports equipment, or a veneer.