Steel wire rod enabling omission of softening heat treatment and method of manufacturing same
The present disclosure relates to a steel wire rod enabling the omission of softening heat treatment and a method of manufacturing same. An embodiment of the present disclosure provides a steel wire rod enabling the omission of softening heat treatment and a method of manufacturing same, the steel wire rod comprising, in weight %, 0.2-0.45% of C, 0.02-0.4% of Si, 0.3-1.5% of Mn, 0.01-1.5% of Cr, 0.02-0.05% of Al, 0.01-0.5% of Mo, 0.01% or less of N, and the balance Fe and other unavoidable impurities, wherein the microstructure of the steel wire rod is a composite structure of proeutectoid ferrite+perlite as a main phase; the steel wire rod contains 10 area % or less (including 0%) of at least one of bainite or martensite; and the average colony size of the perlite is 5 μm or less.
1. A steel wire rod enabling omission of softening heat treatment, the steel wire rod comprising:
by weight %, 0.2-0.45% of C, 0.02-0.4% of Si, 0.3-1.5% of Mn, 0.01-1.5% of Cr, 0.02-0.05% of Al, 0.01-0.5% of Mo, 0.01% or less of N, and a balance Fe and other inevitable impurities,
wherein a microstructure has a main phase of a composite structure of proeutectoid ferrite+pearlite, and includes 10 area % or less of one or more of bainite or martensite, and
wherein an average colony size of pearlite is 5 μm or less.
2. The steel wire rod of claim 1 , wherein a fraction of proeutectoid ferrite is 80% or more of an equilibrium phase.
3. The steel wire rod of claim 1 , wherein, in the steel wire rod, an average grain size of proeutectoid ferrite is 7 μm or less.
4. The steel wire rod of claim 1 , wherein, in the steel wire rod, an average size of a long axis of cementite in pearlite colony is 5 μm or less.
5. The steel wire rod of claim 1 , wherein the steel wire rod has tensile strength of 800 MPa or less.
6. The steel wire rod of claim 1 , wherein, in the steel wire rod, an average aspect ratio of cementite is 2.5 or less after a spheroidization heat treatment is performed once.
7. The steel wire rod of claim 1 , wherein the steel wire rod has tensile strength of 540 MPa or less after a spheroidization heat treatment is performed once.