Cemented carbide for high demand applications
View Patent ↗Provided is a corrosion, erosion and wear resistant cemented carbide for high demand applications including, for example, use as a component within oil and gas production. The cemented carbide includes a hard phase and a binder phase. The cemented carbide may include, for example. Ni, Cr and Mo. The binder phase content of the cemented carbide is between 7 to 11 wt %. The WC of the cemented carbide may have an average grain size of from 0.1 to 2 μm.
1. A cemented carbide having a hard phase and a binder phase, the cemented carbide consisting of:
Ni present in an amount of 7.50 by weight (wt.)% based on a total amount of the cemented carbide;
Cr present in an amount of 0.75 by wt. % based on a total amount of the cemented carbide;
Mo present in an amount of 0.75 by wt. % based on a total amount of the cemented carbide; and
WC present in an amount of 91 by wt. % based on a total amount of the cemented carbide,
wherein the binder phase is present in an amount of 9 by wt. % based on a total amount of the cemented carbide, and
wherein the WC has a grain size of 1 μm.
2. The cemented carbide of claim 1 , wherein a quotient of Cr/(Ni+Cr+Mo) in the cemented carbide is from 0.03 to 0.10.
3. The cemented carbide of claim 1 , wherein a quotient of Mo/(Ni+Cr+Mo) in the cemented carbide is in a range of from 0.04 to 0.12.
4. A component selected from the group consisting of a choke valve, a control valve, a valve seat, a plug seat, a frac seat, a cage, a cage assembly, a seal ring, and a component part of a valve to allow the through-flow of a fluid and a slurry, the component comprising the cemented carbide of claim 1 .
5. A method of making a cemented carbide article having a hard phase and a binder phase, the method comprising:
preparing a powdered batch consisting of raw materials in weight (wt.)% of 7.50 Ni; 0.75 Cr; 0.75 Mo; and 91 WC based on a total amount of the powdered batch;
pressing the powdered batch to form a pre-form; and
sintering the pre-form to form the cemented carbide article,
wherein the binder phase of the cemented carbide article is present in an amount of 9 by wt. % based on a total amount of the cemented carbide article, and the WC included in the powdered batch has a particle size of 0.4 μm to 2 μm determined by Fisher sub sieve sizer (FSSS), and
wherein the sintered WC has a grain size of 1 μm.
6. The method of claim 5 , wherein the sintering the pre-form to form the cemented carbide article comprises vacuum or HIP processing.
7. The method of claim 5 , wherein the sintering comprises processing at a temperature 1360° C.-1500° C. and a pressure 0-20 MPa.