Cemented carbide for high demand applications
View Patent ↗Provided is a corrosion and erosion resistant cemented carbide for high demand including, for example, oil and gas flow applications. The cemented carbide grade may include, for example, including the following constituents Co, Ni, Cr, Mo and WC. The binder phase content of the cemented carbide is between 5.1 to 7.5 wt %. The wt % of Co in the cemented carbide may be less than the wt % of Ni.
1. A cemented carbide having a hard phase and a binder phase, the cemented carbide consisting of:
Co present in an amount of 2.3 by wt. % of the cemented carbide;
Ni present in an amount of 3.5 by wt. % of the cemented carbide;
Cr 3 C 2 present in an amount of 1.0 by wt. % of the cemented carbide;
Mo present in an amount of 0.2 by wt. % of the cemented carbide; and
WC present in an amount of 93.0 by wt. % of the cemented carbide,
wherein the binder phase is present in an amount of from 5.1 to 7.5 by wt. % of the cemented carbide.
2. The cemented carbide of claim 1 , wherein a wt. % quotient of Cr/(Co+Ni+Cr+Mo) in the cemented carbide is in a range of from 0.08 to 0.14.
3. The cemented carbide of claim 1 , wherein a wt. % quotient of Mo/(Co+Ni+Cr+Mo) in the cemented carbide is in a range of from 0.01 to 0.06.
4. The cemented carbide of claim 1 , wherein the WC has a grain size in a range of from 0.2 to 2 μm determined by linear intercept.
5. The cemented carbide of claim 4 , wherein the grain size of the WC is in a range of from 0.3 to 0.9 μm determined by linear intercept.
6. A component, comprising a cemented carbide of claim 1 .
7. The component of claim 6 , comprising a choke valve, a control valve, a valve seat, a plug seat, a frac seat, a cage, a cage assembly, a seal ring, or a component part of a valve to allow the through-flow of a fluid or a slurry.
8. A tool, comprising the cemented carbide of claim 1 .
9. A method of making a cemented carbide article having a hard phase and a binder phase, the method comprising:
preparing a powdered batch comprising Co, Ni, Cr 3 C 2 , Mo, and WC;
pressing the powdered batch to form a pre-form; and
sintering the pre-form to form the cemented carbide article,
wherein the binder phase of the cemented carbide article is present in an amount of from 5.1 to 7.5 by wt. % of the cemented carbide article, and
wherein the sintered cemented carbide article has a cemented carbide composition consisting of Co present in an amount of 2.3 by wt. % of the cemented carbide composition, Ni present in an amount of 3.5 by wt. % of the cemented carbide composition, Cr 3 C 2 present in an amount of 1.0 by wt. % of the cemented carbide composition, Mo present in an amount of 0.2 by wt. % of the cemented carbide composition, and WC present in an amount of 93.0 by wt. % of the cemented carbide composition.
10. The method of claim 9 , wherein the sintering the preform to form the article comprises vacuum or HIP processing.
11. The method of claim 9 , wherein the sintering comprises processing at a temperature 1360-1500° C. and a pressure 0-20 MPa.