Lithium metal anode, method for manufacturing same, and lithium secondary battery using same

1. A lithium metal anode, comprising

a current collector having a flat structure, and

an anode active material layer including a lithium metal disposed on the current collector, and

the lithium metal has a concavo-convex structure,

wherein no dendrite is present on the surface of the lithium metal,

provided that the dendrite refers to a particle in which a ratio of the longest length of the particle in one direction and a length in the direction perpendicular to the longest length of the particle is greater than or equal to 3,

wherein based on a planar projection area of the lithium metal, the lithium metal has pores of 5% to 30% with respect to an entire planar projection area,

wherein a depth of the concavo-convex structure in a thickness direction is 20% to 100% based on total thickness of lithium metal,

wherein a minimum depth of the concavo-convex structure in a thickness direction is 20% to 50%, and

wherein a maximum depth of the concavo-convex structure in a thickness direction is 100%.

2. The lithium metal anode of claim 1 , wherein

in the lithium metal,

a depth of the concavo-convex structure is 20% to 50% based on the total thickness of the lithium metal.

3. The lithium metal anode of claim 1 , wherein

in the lithium metal,

an interval of the concavo-convex is 5 μm to 100 μm.

4. The lithium metal anode of claim 1 , wherein thickness of the lithium metal is 1 μm to 100 μm.

5. The lithium metal anode of claim 1 , wherein a film is further included on a surface of the anode active material layer.

6. The lithium metal anode of claim 5 , wherein the film is a Li—N—C—H—O-based ionic compound, a Li—P—C—H—O-based ionic compound, LiF, or a combination thereof.

7. A lithium secondary battery, comprising

a cathode;

an anode; and

an electrolyte between the cathode and anode, and

the anode is the anode of claim 1 .

8. A method of manufacturing lithium metal anode, comprising

preparing a current collector and a lithium source opposed thereto, which are impregnated in an electrolyte solution; and

applying a current to the current collector and the lithium source to electroplate lithium metal on a surface of the current collector,

wherein in applying of the current to the current collector and the lithium source to electroplate lithium metal on the surface of the current collector,

the current application is performed through two steps, and

a current density at second current application is higher than a current density at first current application,

wherein the current density at the first current application is 0.2 mA/cm 2 to 0.8 mA/cm 2 .

9. The method of claim 8 , wherein the current density at the second current application is 1 mA/cm 2 to 4 mA/cm 2 .

10. The method of claim 8 , wherein the second current application time is longer than the first current application time.

11. The method of claim 10 , wherein the first current application time is 1 hour to 4 hours.

12. The method of claim 10 , wherein the second current application time is 1 hour to 24 hours.