Latex and latex articles formed from branched polymers
Dipped formed latex articles with improved properties are formed from branched block copolymers, derived from alkenyl aromatic hydrocarbon—1,3-diene monomer system, and branched polyisoprene homopolymers, derived from isoprene. The polymers are obtained by polymerization in the presence of an anionic initiator; at a temperature from 0° C. to 100° C.; followed by coupling with a multifunctional coupling agent of formula (R 1 O) 3 Si—Y—Si(OR 2 ) 3 , wherein R 1 and R 2 are independently C 1 -C 6 alkyl groups; and Y is a C 2 -C 8 alkylene group. The polymers are obtained as rubber cements having high solids content and low zero shear viscosities. The rubber cements are valuable for making latices and latex articles such as dipped goods, e.g., condoms, gloves, etc., with improved properties.
1. A film article made of a latex comprising a branched polyisoprene homopolymer having a formula (C) m (R 1 O) 3-m Si—Y—Si(R 2 O) 3-n (C) n ,
wherein
each C block is independently a polyisoprene block having a weight average molecular weight from 400-1000 kg/mol;
R 1 and R 2 are independently H, or C 1 -C 6 alkyl groups; Y is a C 2 -C 8 alkylene group; m and n are integers independently having values from 1-3,
the branched polyisoprene homopolymer has a coupling efficiency (CE) of at least 40%; and
wherein
the film article exhibits a tensile strength of at least 20 MPa.
2. The film article of claim 1 , wherein (m+n) has a value from 3-6.
3. The film article of claim 1 , wherein Y is —CH 2 CH 2 —, and R 1 and R 2 are hydrogen, methyl groups or ethyl groups.
4. The film article of claim 1 , wherein the C block has a weight average molecular weight from 500-700 kg/mol.
5. The film article of claim 1 , wherein the film article exhibits at least one of an elongation at break of at least 500%, and a tear strength of at least 15 kN/m.