Synthesis, capping, and dispersion of TiO
The preparation of monodispersed TiO 2 nanocrystals with nanocrystal size between 1-30 nm is described herein. These TiO 2 nanocrystals are used to prepare dispersions into solvents, formulation into monomers, oligomers, and polymers, and nanocomposites from the resulting formulations. Dispersions of nanocrystals can be formed in various solvents at high loading, high transmittance, and low viscosity. Formulations incorporating these nanocrystals and a matrix material are highly stable, where the resulting nanocomposites have high refractive index and are optically transparent in the visible wavelengths, with very little or no scattering.
1. At least partially capped TiO2 nanocrystals comprising TiO 2 nanocrystals at least partially capped with at least one capping agent selected from a silane, an alcohol, a carboxylic acid, a thiol, a sulfonate, a phosphonate, a phosphate, and combinations thereof, wherein the TiO 2 nanocrystals have an average particle size of about 4 nm to about 50 nm as measured by TEM, wherein the TiO2 nanocrystals have anatase crystalline structure,
wherein the particle size distribution of the at least partially capped TiO2 nanocrystals is characterized by a D9999 of less than 500 nm as measured by volume by DLS when measured as a 5% dispersion in a solvent.
2. A nanocrystal dispersion comprising at least partially capped TiO 2 nanocrystals and a solvent, wherein the at least partially capped TiO 2 nanocrystals are present in an amount of greater than 30%, by weight of the dispersion, having an average particle size in the range of 4-50 nm as measured by TEM, wherein the D9999 of the TiO 2 nanocrystals in the dispersion, as determined by DLS, is in the range of 20-500 nm when measured as a 5% nanocrystal dispersion in the solvent.
3. A nanocomposite formulation comprising 1) the at least partially capped TiO 2 nanocrystals of claim 1 ; 2) a monomer, oligomer, and/or polymer; and 3) a curing agent, wherein the at least partially capped TiO 2 nanocrystals are present in an amount of greater than 50% by weight in respect to the monomer, oligomer and/or polymer.
4. A method of coating a substrate, comprising applying the nanocomposite formulation of claim 3 to the surface of the substrate, and optionally curing the nanocomposite formulation.
5. The coated substrate produced by the method of claim 4 .
6. A nanocomposite film comprising the at least partially capped TiO 2 nanocrystals of claim 1 and at least one monomer, oligomer and/or polymer, wherein the at least partially capped nanocrystals are present in an amount greater than 30%, by weight of the nanocomposite, wherein the transmittance of the film with a thickness of 1 micron is greater than 80% at wavelength of 400 nm, and the film has a refractive index of about 1.70 to about 2.10 as measured using a Prism Coupler of a film with <5 μm thickness.
7. The nanocomposite film of claim 6 , having a hardness of greater than 100 MPa, as measured by nanoindentation.
8. A method of preparing the nanocomposite film of claim 6 , the method comprising mixing the at least partially capped TiO 2 nanocrystals and at least one monomer, oligomer and/or polymer to provide a nanocomposite formulation, and optionally curing the nanocomposite formulation to provide the nanocomposite film.
9. A device comprising the nanocomposite film of claim 6 .
10. The device of claim 9 , which is an optoelectronic device, photovoltaic device, catalysis device, fuel cell, battery, smart window, sensor, CMOS sensor, LED, mini-LED, microLED, organic LED (OLED), Quantum LED (QLED), touch screen, display, flexible electronic device, printed electronic device, augmented reality, virtual reality, mixed reality, wave guide, diffraction grating or a solar cell device.
11. A device comprising the coated substrate of claim 5 .
12. The device of claim 11 , which is an optoelectronic device, photovoltaic device, catalysis device, fuel cell, battery, smart window, sensor, CMOS sensor, LED, mini-LED, microLED, organic LED (OLED), Quantum LED (QLED), touch screen, display, flexible electronic device, printed electronic device, augmented reality, virtual reality, mixed reality, wave guide, diffraction grating or a solar cell device.
13. The at least partially capped TiO2 nanocrystals of claim 1 wherein the organic content of the at least partially capped TiO 2 nanocrystals is 5% to 35%, as measured by TGA.
14. The at least partially capped TiO2 nanocrystals of claim 1 capped with at least one capping agent selected from methyltrimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, noctyltrimethoxysilane, n-octyltriethoxysilane, phenytrimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl] trimethoxysilane, methoxy(triethyleneoxy)propyltrimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, 3-(acryloyloxy)propyl trimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, 3-glycidoxypropyltrimethoxysilane, vinyltrimethoxysilane, allyltrimethoxysilane, 1-hexenyltrimethoxysilane, 1-octenyltrimethoxysilane, (phenylaminomethyl) methyldimethoxysilane, N-phenylaminopropyltrimethoxysilane, 3-(4-pyridylethyl)thiopropyltrimethoxysilane, N-(3-trimethoxysilylpropyl)pyrrole, 2-(3-trimethoxysilylpropylthio) thiophene, (3-trimethoxysilylpropyl)diethylene triamine, 11-mercaptoundecyltrimethoxysilane, (2-diphenylphosphino) ethyldimethylethoxysilane, 2-(diphenylphosphino) ethyltriethoxysilane, 3-(diphenylphosphino) propyltriethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol, triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, 2-[2-(2-methoxyethoxy)ethoxy] acetic acid, oleic acid, benzoic acid, stearic acid, trifluoroacetic acid, biphenyl-4-carboxylic acid, 2-(2-methoxyethoxy) acetic acid, methacrylic acid, mono-2-(Methacryloyloxy)ethyl succinate, 2-mercaptoethanol, 2-{2-[2-(2-mercaptoethoxy) ethoxy]ethoxy} ethanol, 2-(2-methoxyethoxy)ethanethiol, 1-octanethiol, sodium 2,3-dimercaptopropanesulfonate monohydrate, sodium dodecyl sulfate, dodecyl phosphonic acid, octylphosphonic acid, (11-mercaptoundecyl)phosphonic acid, (11-(acryloyloxy)undecyl)phosphonic acid, 11-methacryloyloxyundecylphosphonic acid, [2-[2-(2-methoxyethoxy)ethoxy]ethyl]phosphonic acid ethyl ester, and combinations thereof.
15. The at least partially capped TiO 2 nanocrystals of claim 1 , capped with at least one capping agent selected from methyltrimethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, methoxy(triethyleneoxy)propyltrimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, 3-(acryloyloxy)propyl trimethoxysilane, 3-glycidoxypropyltrimethoxysilane, vinyltrimethoxysilane, allyltrimethoxysilane, octanol, benzyl alcohol, ethanol, propanol, butanol, oleylalcohol, octanoic acid, acetic acid, 2-[2-(2-methoxyethoxy) ethoxy] acetic acid, oleic acid, benzoic acid, stearic acid, trifluoroacetic acid, 2-(2-methoxyethoxy) acetic acid, methacrylic acid, mono-2-(Methacryloyloxy)ethyl succinate, 2-mercaptoethanol, 2-{2-[2-(2-mercaptoethoxy) ethoxy]ethoxy} ethanol, 2-(2-methoxyethoxy)ethanethiol, dodecyl phosphonic acid, octylphosphonic acid, (11-mercaptoundecyl)phosphonic acid, (11-(acryloyloxy)undecyl)phosphonic acid, 11-methacryloyloxyundecylphosphonic acid, [2-[2-(2-methoxyethoxy)ethoxy]ethyl] phosphonic acid ethyl ester, and combinations thereof.
16. The at least partially capped TiO 2 nanocrystals of claim 1 , wherein the D9999 is less than 400 nm, as measured by volume of the capped titanium dioxide nanocrystals dispersed 5% by weight in the solvent by Dynamic Light Scattering (DLS).
17. The nanocomposite formulation of claim 3 , further comprising a solvent.
18. The nanocomposite formulation of claim 3 , wherein the monomer, oligomer and/or polymer is an acrylate, epoxy, or isocyanurate compound, selected from Bisphenol A Glycerolate Dimethacrylate, esters with acrylic acid (OPPEOA), Bisphenol A Ethoxylate diacrylates, Bisphenol A propoxylate diacrylate, Bisphenol F ethoxylate (2 EO/phenol) diacrylate, Bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, Ethoxylated (4) bisphenol A diacrylate (SR-601), Biphenol A ethoxylate diacrylate (SR-349), Tris(2-acryloyloxy)ethyl} isocyanurate, tricyclodecane dimethanol diacrylate, Tris (2-hydroxyethyl)isocyanurate triacrylate, cresol novolac epoxy acrylate (CN112C60), Benzyl methacrylate (BMA), benzyl acrylate, trimethylolpropane triacrylate (TMPTA), Trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-Hexanediol diacrylate (HDDA, SR238B), tri (ethyleneglycol) diacrylate, ethylene glycol diacrylate, Poly (ethylene glycol) diacrylate, Glycerol 1,3-diglycerolate diacrylate, Di(ethylene glycol) diacrylate, and combinations thereof.
19. The nanocomposite film of claim 6 , wherein the % transmittance of the film with a thickness of 1 micron is greater than 80%, at wavelength of 400 nm.
20. The nanocomposite film of claim 6 , having a refractive index of 1.70 to 2.10 at 635 nm, as measured using a Prism Coupler of a film with <5 μm thickness.
21. The nanocomposite film of claim 6 , having a hardness of greater than 50 MPa, as measured by nanoindentation.
22. The nanocomposite film of claim 6 , wherein the haze of the nanocomposite film is less than 1%, and wherein the at least partially capped nanocrystals are dispersed without agglomeration in the film as observed by TEM, SEM or EDX images.