Prills of hydroquinone and method for obtaining the same
The present invention relates to new lightly colored prills of hydroquinone. More particularly, the invention provides a new method for preparing said lightly colored prills of hydroquinone. The invention also relates to said prills of hydroquinone obtained by said new method.
1. A process for the preparation of prills of hydroquinone comprising:
a) providing molten hydroquinone,
b) forcing said molten composition through at least one droplet generator means to form droplets,
c) cooling said droplets to form solid hydroquinone prills having a color in 5% aqueous solution of less than 250 Hazen and wherein the water content is from 0.1 wt % to 10 wt %.
2. The process according to claim 1 wherein the molten hydroquinone comprises less than 10 wt. % of water.
3. The process according to claim 1 , wherein the molten hydroquinone further comprises at least one other compound.
4. The process according to claim 1 wherein the molten hydroquinone further comprises at least one polymerization inhibitor.
5. The process according to claim 1 wherein steps a), b) and/or c) are conducted under inert gas, or oxygen-depleted air.
6. The process according to claim 1 wherein step a) is conducted at a temperature of 1 to 50° C. above the melting point of hydroquinone.
7. The process according to claim 1 wherein step b) is conducted at a temperature of 1 to 50° C. above the melting point of hydroquinone.
8. The process according to claim 1 wherein an overpressure of 5% to 2000% with respect to atmospheric pressure is applied in step b).
9. The process according to claim 1 wherein the cooling medium temperature is maintained at a temperature of between −196° C. and +150° C.
10. The process according to claim 1 , wherein the hydroquinone prills have an internal porosity from 0.1 cm 3 /g to 0.75 cm 3 /g, a loose apparent density of at least 0.3, a compact apparent density of at least 0.5, a friability of less than 15%, a hardness of at least 0.7N, or an angle of repose between 20° and 40°.
11. The process according to claim 1 , wherein the hydroquinone prills have a d 50 between 0.3 mm and 1 cm.
12. The process according to claim 1 , wherein the hydroquinone prills have a particle size distribution where at least 50% of particle have a size between 300 μm and 2000 μm.
13. The process according to claim 1 , wherein the hydroquinone prills do not cake when stored at 50° C. during 7 days.
14. The process according to claim 1 , wherein the hydroquinone prills comprise at least one other compound.
15. The process according to claim 1 , wherein the hydroquinone prills comprise at least one polymerization inhibitor.
16. The process according to claim 1 , wherein, when discharged, the amount of dust produced is at least reduced by 20% compared to the amount of dust produced when hydroquinone powder is discharged.