High strength hot rolled steel sheet having excellent elongation and method for manufacturing the same
The present invention provides a high strength hot rolled steel sheet and a method for manufacturing same, the steel sheet containing, in weight percentage, 0.11-0.14% of C, 0.20-0.50% of Si, 1.8-2.0% of Mn, 0.03% or less of P, 0.02% or less of S, 0.01-0.04% of Nb, 0.5-0.8% of Cr, 0.01-0.03% of Ti, 0.2-0.4% of Cu, 0.1-0.4% of Ni, 0.2-0.4% of Mo, 0.007% or less of N, 0.001-0.006% of Ca, 0.01-0.05% of Al, a balance of Fe and inevitable impurities, wherein relational expressions 1 to 3 below are satisfied, and a microstructure includes, by area percentage, 88% or more of bainite, 10% or less of ferrite, 2% or less of pearlite, and 0.8% or less of island martensite. [Relational Expression 1] 7≤(Mo/93)/(P/31)≤16. [Relational Expression 2] 1.6≤Cr+3Mo+2Ni≤2. [Relational Expression 3] 6≤(3C/12+Mn/55)×100≤7.
1. A hot rolled steel sheet-having excellent elongation, comprising:
by wt %, 0.11 to 0.14% of C, 0.20 to 0.50% of Si, 1.8 to 2.0% of Mn, 0.03% or less of P, 0.02% or less of S, 0.01 to 0.04% of Nb, 0.5 to 0.8% of Cr, 0.01 to 0.03% of Ti, 0.2 to 0.4% of Cu, 0.1 to 0.4% of Ni, 0.2 to 0.4% of Mo, 0.007% or less of N, 0.001 to 0.006% of Ca, 0.01 to 0.05% of Al, a balance of Fe, and inevitable impurities,
wherein relational expressions 1 to 3 below are satisfied, and
a microstructure comprises, by area %, 88% or more of bainite, excluding 100%, 10% or less of ferrite, excluding 0%, 2% or less of pearlite, excluding 0%, and 0.8% or less of martensite-austenite constituent, inclusive of 0%,
7≤(Mo/93)/(P/31)≤16 [Relational Expression 1]
1.6≤Cr+3Mo+2Ni≤2 [Relational Expression 2]
6≤(3C/12+Mn/55)×100≤7 [Relational Expression 3]
where, in relational expressions 1 to 3, the contents of alloying elements are based on wt %.
2. The hot rolled steel sheet of claim 1 , wherein an average grain size of the bainite is 8 μm or less.
3. The hot rolled steel sheet of claim 1 , wherein an average grain size of the ferrite is 10 μm or less.
4. The hot rolled steel sheet of claim 1 , wherein an average grain size of the pearlite is 4 μm or less.
5. The hot rolled steel sheet of claim 1 , wherein an average grain size of the martensite-austenite constituent is 1 μm or less.
6. The hot rolled steel sheet of claim 1 , wherein the hot rolled steel sheet has a yield strength of 850 MPa or more at room temperature, a tensile strength of 900 MPa or more at room temperature, and a total elongation of 13% or more.