Interference pigments
The invention relates to interference pigments based on SiO 2 flakes having a broad layer-thickness distribution, and to the use thereof in paints, coatings, powder coatings, plastics and in particular in cosmetic formulations and for colouring food and pharmaceutical products.
1. Interference pigment based on a substrate mixture, wherein the substrate mixture consists of SiO 2 flakes, which SiO 2 flakes have at least 4 different thicknesses, and which SiO 2 flakes are coated with at least one high-refractive-index layer.
2. The interference pigment according to claim 1 , wherein the SiO 2 flakes have 4, 5, 6, 7 or 8 different layer thicknesses.
3. The interference pigment according to claim 1 , wherein the SiO 2 flakes differ in layer thicknesses by in each case at least 10 nm.
4. The interference pigment according to claim 1 , wherein the layer thicknesses of the SiO 2 flakes are from 100-1000 nm.
5. The interference pigment according to claim 1 , wherein the substrate mixture contains at least 4 SiO 2 flakes from the following group of SiO 2 flakes:
SiO 2 flakes having a layer thickness of 360 nm
SiO 2 flakes having a layer thickness of 380 nm
SiO 2 flakes having a layer thickness of 400 nm
SiO 2 flakes having a layer thickness of 420 nm
SiO 2 flakes having a layer thickness of 440 nm
SiO 2 flakes having a layer thickness of 460 nm
SiO 2 flakes having a layer thickness of 480 nm
SiO 2 flakes having a layer thickness of 500 nm
or
SiO 2 flakes having a layer thickness of 360 nm
SiO 2 flakes having a layer thickness of 380 nm
SiO 2 flakes having a layer thickness of 400 nm
SiO 2 flakes having a layer thickness of 420 nm
SiO 2 flakes having a layer thickness of 440 nm
SiO 2 flakes having a layer thickness of 460 nm
SiO 2 flakes having a layer thickness of 480 nm
or
SiO 2 flakes having a layer thickness of 300 nm
SiO 2 flakes having a layer thickness of 320 nm
SiO 2 flakes having a layer thickness of 340 nm
SiO 2 flakes having a layer thickness of 360 nm
SiO 2 flakes having a layer thickness of 380 nm
SiO 2 flakes having a layer thickness of 400 nm
SiO 2 flakes having a layer thickness of 420 nm
SiO 2 flakes having a layer thickness of 440 nm
or
SiO 2 flakes having a layer thickness of 300 nm
SiO 2 flakes having a layer thickness of 310 nm
SiO 2 flakes having a layer thickness of 340 nm
SiO 2 flakes having a layer thickness of 350 nm
SiO 2 flakes having a layer thickness of 370 nm
SiO 2 flakes having a layer thickness of 380 nm
or
SiO 2 flakes having a layer thickness of 400 nm
SiO 2 flakes having a layer thickness of 420 nm
SiO 2 flakes having a layer thickness of 440 nm
SiO 2 flakes having a layer thickness of 460 nm
SiO 2 flakes having a layer thickness of 480 nm
SiO 2 flakes having a layer thickness of 500 nm
SiO 2 flakes having a layer thickness of 520 nm.
6. The interference pigment according to claim 1 , wherein the substrate mixture consists of the following SiO 2 flakes:
SiO 2 flakes having a layer thickness of 360 nm
SiO 2 flakes having a layer thickness of 380 nm
SiO 2 flakes having a layer thickness of 400 nm
SiO 2 flakes having a layer thickness of 420 nm
SiO 2 flakes having a layer thickness of 440 nm
SiO 2 flakes having a layer thickness of 460 nm
SiO 2 flakes having a layer thickness of 480 nm
SiO 2 flakes having a layer thickness of 500 nm.
7. The interference pigment according to claim 1 , wherein the substrate mixture is coated with at least one high-refractive-index layer having a refractive index of n>1.8.
8. The interference pigment according to claim 1 , wherein the high-refractive-index layer is selected from the group consisting of metal oxides, BiOCl, metal hydroxides, metals, metal sulfides and mixtures thereof.
9. The interference pigment according to claim 1 , wherein the high-refractive-index layer is selected from the group consisting of TiO 2 , Fe 2 O 3 , FeOOH, Fe 3 O 4 , ZrO 2 , SnO 2 , ZnO, BiOCl and mixtures thereof.
10. The interference pigment according to claim 1 , wherein the flakes are coated with TiO 2 , Fe 2 O 3 , FeOOH, Fe 3 O 4 or a mixture thereof.
11. The interference pigment according to claim 1 , wherein the SiO 2 flakes are coated with at least one high-refractive-index layer and at least one low-refractive-index layer.
12. The interference pigment according to claim 1 , wherein the substrate mixture containing SiO 2 flakes is coated with alternating layers of at least one high-refractive-index layer and at least one low-refractive index layer.
13. The interference pigment according to claim 1 , wherein the low-refractive-index layer is selected from the group consisting of SiO 2 , MgO and MgO*SiO 2 .
14. The interference pigment according to claim 1 , wherein the SiO 2 flakes have a surface coating selected from the group consisting of:
substrate mixture+TiO 2
substrate mixture+Fe 2 O 3
substrate mixture+FeOOH
substrate mixture+Fe 3 O 4
substrate mixture+TiO 2 /Fe 2 O 3
substrate mixture+TiO 2 +Fe 2 O 3
substrate mixture+TiO 2 +FeOOH
substrate mixture+TiO 2 +Fe 3 O 4
substrate mixture+TiO 2 +SiO 2
substrate mixture+Fe 2 O 3 +SiO 2
substrate mixture+FeOOH+SiO 2
substrate mixture+Fe 3 O 4 +SiO 2
substrate mixture+TiO 2 +SiO 2 /Al 2 O 3
substrate mixture+TiO 2 +Al 2 O 3
substrate mixture+Fe 2 O 3 +Al 2 O 3
substrate mixture+FeOOH+Al 2 O 3
substrate mixture+Fe 3 O 4 +Al 2 O 3
substrate mixture+Cr 2 O 3
substrate mixture+SnO 2
substrate mixture+SiO 2
substrate mixture+ZrO 2
substrate mixture+ZnO
substrate mixture+TiO 2 +SiO 2 +TiO 2
substrate mixture+TiO 2 +Al 2 O 3 +TiO 2
substrate mixture+TiO 2 +MgO*SiO 2 +TiO 2
substrate mixture+TiO 2 +CaO*SiO 2 +TiO 2
substrate mixture+TiO 2 +Al 2 O 3 *SiO 2 +TiO 2
substrate mixture+TiO 2 +B 2 O 3 *SiO 2 +TiO 2
substrate mixture+Fe 2 O 3 +SiO 2 +TiO 2
substrate mixture+Fe 2 O 3 +SiO 2 +TiO 2
substrate mixture+Fe 2 O 3 +SiO 2 +Fe 2 O 3
substrate mixture+Fe 2 O 3 +SiO 2 +SnO 2 +Fe 2 O 3
substrate mixture+Fe 2 O 3 +Al 2 O 3 +TiO 2
substrate mixture+Fe 2 O 3 +Al 2 O 3 +Fe 2 O 3
substrate mixture+Fe 2 O 3 +MgO*SiO 2 +TiO 2
substrate mixture+Fe 2 O 3 +CaO*SiO 2 +TiO 2
substrate mixture+Fe 2 O 3 +Al 2 O 3 *SiO 2 +TiO 2
substrate mixture+Fe 2 O 3 +B 2 O 3 *SiO 2 +TiO 2
substrate mixture+Fe 2 O 3 +MgO*SiO 2 +Fe 2 O 3
substrate mixture+Fe 2 O 3 +CaO*SiO 2 +Fe 2 O 3
substrate mixture+Fe 2 O 3 +Al 2 O 3 *SiO 2 +Fe 2 O 3
substrate mixture+Fe 2 O 3 +B 2 O 3 *SiO 2 +Fe 2 O 3
substrate mixture+TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2
substrate mixture+TiO 2 /Fe 2 O 3 +Al 2 O 3 +TiO 2
substrate mixture+TiO 2 /Fe 2 O 3 +MgO*SiO 2 +TiO 2
substrate mixture+TiO 2 /Fe 2 O 3 +CaO*SiO 2 +TiO 2
substrate mixture+TiO 2 /Fe 2 O 3 +Al 2 O 3 *SiO 2 +TiO 2
substrate mixture+TiO 2 /Fe 2 O 3 +B 2 O 3 *SiO 2 +TiO 2
substrate mixture+TiO 2 +SiO 2 +TiO 2 /Fe 2 O 3
substrate mixture+TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2 /Fe 2 O 3
substrate mixture+TiO 2 /Fe 2 O 3 +MgO*SiO 2 +TiO 2 /Fe 2 O 3
substrate mixture+TiO 2 +Al 2 O 3 +TiO 2 /Fe 2 O 3
substrate mixture+TiO 2 +MgO*SiO 2 +TiO 2 /Fe 2 O 3
substrate mixture+TiO 2 +CaO*SiO 2 +TiO 2 /Fe 2 O 3
substrate mixture+TiO 2 +Al 2 O 3 *SiO 2 +TiO 2 /Fe 2 O 3
substrate mixture+TiO 2 +B 2 O 3 *SiO 2 +TiO 2 /Fe 2 O 3
substrate mixture+TiO 2 +Al 2 O 3 +Fe 2 O 3
substrate mixture+TiO 2 +MgO*SiO 2 +Fe 2 O 3
substrate mixture+TiO 2 +CaO*SiO 2 +Fe 2 O 3
substrate mixture+TiO 2 +Al 2 O 3 *SiO 2 +Fe 2 O 3
substrate mixture+TiO 2 +B 2 O 3 *SiO 2 +Fe 2 O 3
substrate mixture+SnO 2 +TiO 2
substrate mixture+SnO 2 +Fe 2 O 3
substrate mixture+SnO 2 +FeOOH and
substrate mixture+SnO 2 +Fe 3 O 4 .
15. A process for the preparation of the interference pigments according to claim 1 , comprising coating a mixture of SiO 2 flakes having at least 4 different layer thicknesses-is-coated with at least one high-refractive-index layer.
16. A product selected from the group consisting of paints, coatings, printing inks, security printing inks, plastics, ceramic materials, glazes, glasses, cosmetic formulations, pigment preparations, dry preparations, food colouring and pharmaceutical products colouring comprising the interference pigments according to claim 1 .
17. A formulation comprising the interference pigment according to claim 1 .
18. The formulation according to claim 17 , further comprising at least one constituent selected from the group consisting of absorbents, astringents, antimicrobial substances, antioxidants, antiperspirants, antifoaming agents, anti-dandruff active compounds, antistatics, binders, biological additives, bleaches, chelating agents, deodorants, emollients, emulsifiers, emulsion stabilisers, dyes, humectants, film formers, fillers, fragrances, flavours, insect repellents, preservatives, anticorrosion agents, cosmetic oils, solvents, oxidants, plant constituents, buffer substances, reducing agents, surfactants, propellant gases, opacifiers, UV filters, UV absorbers, denaturing agents, aloe vera, avocado oil, coenzyme Q10, green tea extract, viscosity regulators, perfume, vitamins, enzymes, trace elements, proteins, carbohydrates, essential fats, minerals, natural dyes, nature-identical dyes, vegetable black, acids, sugars, fats, flavour enhancers, dyes, flavours, sweeteners, colouring fruit extracts, colouring plant extracts, cocoa, wax, gum arabic, cellulose, cellulose derivatives, starch, spirulina, albumen, albumen derivatives, and carrageenan.