Steel plate for high temperature applications having excellent strength at high temperature and method for manufacturing the same
Provided are a steel plate for high temperature applications having excellent strength at a high temperature and a method for manufacturing same. The steel plate for high temperature applications having excellent post-weld heat treatment resistance, according to the present invention, comprises by weight percent: C:0.05-0.25%; Mn:0.1-1.0%; Si:0.1-0.8%; Cr:1-3%; Cu:0.05-0.3%; Mo:0.5-1.5%; Ni:0.05-0.5%; Al:0.005-0.1%; and at least one of Ir:0.005-0.10% and Rh:0.005-0.10%, the balance being Fe and inevitable impurities.
1. A steel plate for high temperature applications having excellent post weld heat treatment (PWHT) resistance, comprising, by wt %:
0.05 to 0.25% of C,
0.1 to 1.0% of Mn,
0.1 to 0.8% of Si,
1 to 3% of Cr,
0.05 to 0.3% of Cu,
0.5 to 1.5% of Mo,
0.05 to 0.5% of Ni,
0.005 to 0.1% of Al,
one or more of 0.005 to 0.10% of Ir and 0.005 to 0.10% of Rh,
a balance of Fe, and
inevitable impurities,
wherein the steel plate has a microstructure comprised of 50 area % or more of tempered martensite, and a remainder of residual tempered bainite.
2. The steel plate of claim 1 , wherein the microstructure includes a grain that includes fine oxide of either IrO 2 or Rh 2 O 3 , and the fine oxide has a size of 1 μm or less.
3. The steel plate of claim 2 , wherein the oxide has an area fraction of 0.015% or more.
4. The steel plate of claim 1 , wherein the steel plate has a high-temperature tensile strength of 400 MPa or more at 500° C. even after PWHT for 100 hours.
5. The steel plate of claim 1 , comprising, by wt %, 0.005 to 0.10% of Rh.
6. The steel plate of claim 1 , wherein the steel plate has a microstructure consisting of 50 area % or more of tempered martensite, and a remainder of residual tempered bainite.