Non-directional electrical steel sheet and method for producing same
A non-oriented electrical steel sheet according to an embodiment of the present invention includes, in wt %, Si at 0.2 to 4.3%, Mn at 0.05 to 2.5%, Al at 0.1 to 2.1%, Bi at 0.0001 to 0.003%, Ga at 0.0001 to 0.003%, and the balance of Fe and inevitable impurities.
1. A non-oriented electrical steel sheet including, in wt %, Si at 0.2% to 4.3%, Mn at 0.05% to 2.5%, Al at 0.1% to 2.1%, Bi at 0.0003% to 0.003%, Ga at 0.0005% to 0.003%, and a balance of Fe and inevitable impurities,
wherein the non-oriented electrical steel sheet satisfies Formula 2:
−0.002≤[Bi]+[Ga]≤0.005, [Formula 2]
wherein in Formula 2, [Bi] and [Ga] represent content by wt % of Bi and Ga, respectively.
2. The non-oriented electrical steel sheet of claim 1 , wherein
the non-oriented electrical steel sheet satisfies Formula 1:
[Iron loss (W 15/50 ) after shearing processing]−[Iron loss (W 15/50 ) after discharge processing]≤0.05 (W/kg). [Formula 1]
3. The non-oriented electrical steel sheet of claim 1 , wherein
one or more of C, S, N, and Ti are further included in an amount of 0.005 wt % or less, respectively.
4. The non-oriented electrical steel sheet of claim 1 , wherein
one or more of P, Sn, and Sb are further included in an amount of 0.2 wt % or less, respectively.
5. The non-oriented electrical steel sheet of claim 1 , wherein
one or more of Cu, Ni, and Cr are further contained in an amount of 0.05 wt % or less, respectively.
6. The non-oriented electrical steel sheet of claim 1 , wherein
one or more of Zr, Mo, and V are further contained in an amount of 0.01 wt % or less, respectively.