Pelletized activated carbon and methods of production
Activated carbon for removal of sulfur containing materials from fluids. The activated carbon has a high sulfur capacity and can be manufactured without the addition of a catalyst. Lignite is treated to provide an activated carbon with a high mesoporosity and total surface area. The starting material has a high ash content, such as greater than 10% by weight.
1. Filtration media comprising:
activated carbon void of added catalyst and having a hydrogen sulfide capacity of at least 0.2 g/mL when tested using ASTM 6646.
2. The filtration media of claim 1 wherein the activated carbon is derived from lignite including at least 10% ash by weight.
3. The filtration media of claim 1 wherein the activated carbon is activated carbon pellets.
4. The filtration media of claim 3 wherein the activated carbon pellets comprise a binder.
5. The filtration media of claim 4 wherein the binder comprises a carbonized binder.
6. The filtration media of claim 1 wherein the activated carbon consists essentially of twice activated lignite.
7. The filtration media of claim 1 having a ball-pan hardness by ASTM D3802 of greater than or equal to 60 mass %.
8. The filtration media of claim 1 wherein the activated carbon has a minimum mesopore volume of 0.20 cm 3 /g and the ash of the activated carbon includes three different metal oxides, each at a concentration of greater than 1% by weight.
9. The filtration media of claim 1 wherein the activated carbon has a BET surface area of greater than 350 m 2 /g.
10. A method comprising:
passing a fluid comprising hydrogen sulfide through activated carbon, the activated carbon comprising an activated carbon essentially free of added catalyst and having a hydrogen sulfide capacity of at least 0.2 g/mL when tested using ASTM 6646; and
removing hydrogen sulfide from the fluid.
11. The method of claim 10 wherein the fluid is a mixture of gases.
12. The method of claim 10 wherein the fluid is a liquid.
13. The method of claim 10 wherein the activated carbon is derived from coal having an ash content of greater than 10% by weight.
14. The method of claim 10 wherein the activated carbon is in the form of pellets.
15. The method of claim 10 wherein the activated carbon is derived from lignite activated carbon.
16. The method of claim 14 wherein the activated carbon pellets include pellets having at least one dimension greater than 3 mm.
17. The method of claim 10 wherein greater than 90%, 95% or 99% of the hydrogen sulfide, by mass, is removed from the fluid in a single pass.
18. The method of claim 10 wherein at least one additional compound comprising sulfur is substantially removed from the fluid.
19. The method of claim 10 wherein an ash analysis of the activated carbon pellets shows greater than 1% calcium oxide, greater than 1% magnesium oxide and greater than 1% iron oxide.