Polypropylene composition for film sealing layer
New polypropylene composition which combines low sealing initiation temperature (SIT), low overall migration, good mechanical and optical properties, its use and articles made therefrom.
1. Polypropylene composition (PP) comprising a blend of:
(a) 75.0 to 95.0 wt % of a propylene-ethylene random copolymer (A) having:
(a1) ethylene content in the range of from 1.5 to 6.0 wt %;
(a2) MFR 2 , 230° C., 2.16 kg, ISO1133, in a range of from 1.5 to 20.0 g/10 min;
(a3) melting temperature Tm, DSC, is in the range of from 135° C. to 155° C.; and
(b) 5.0 to 25.0 wt % of a component (B) selected from a propylene-hexene random copolymer (B1) having:
(b1) hexene content in the range of from 3.0 to 5.5 wt %;
(b3) MFR 2 , 230° C., 2.16 kg, ISO1133, in a range of from 1.5 to 20.0 g/10 min;
(b4) melting temperature Tm, DSC, in the range of from 125° C. to 145° C., based on the total weight of the sum of the component (A) and component (B), whereby the MFR 2 , 230° C., 2.16 kg, ISO1133, of the blend is in a range of from 1.5 to 20.0 g/10 min, and a weight ratio of component (A) and component (B) is from 3:1 to 12:1.
2. Polypropylene composition (PP) according to claim 1 , wherein the propylene-ethylene random copolymer (A) has a xylene cold soluble (XCS) amount in the range of 3.5 to 10.0 wt %, as measured according to ISO 16152, first edition, 2005, at 25° C.
3. Polypropylene composition (PP) according to claim 1 , wherein the composition has a melting temperature in the range of from 130° C. to 145° C. as measured by differential scanning calorimetry, DSC, according to ISO 11357.
4. Polypropylene composition (PP) according to claim 1 , wherein the composition has a hexane extractable fraction as determined according to the FDA method, federal registration, title 21, Chapter 1, part 177, section 1520, Annex B, on cast films of 100 μm thickness produced on a monolayer cast film line with a melt temperature of 220° C. and a chill roll temperature of 20° C., the extraction being performed at a temperature of 50° C. and an extraction time of 30 min, of not higher than 3.20 wt %.
5. Polypropylene composition (PP) according to claim 1 , wherein the weight ratio of component (A) and component (B) is from 3:1 to 10:1.
6. Polypropylene composition (PP) according to claim 1 , wherein the composition has a xylene cold soluble (XCS) amount in the range of from 8.0 to 15.0 wt %, measured according to ISO 16152, first edition, 2005, at 25° C.
7. Process for the preparation of the polypropylene composition according to claim 1 , the process comprising:
(i) preparing the propylene-ethylene random copolymer (A) by polymerizing propylene and ethylene in the presence of a Ziegler-Natta catalyst;
(ii) preparing the propylene-hexene random copolymer (B1), the propylene-hexene-ethylene terpolymer (B2) or a mixture thereof by polymerizing propylene and hexene and optionally ethylene in the presence of a single site catalyst;
(iii) mixing said propylene-ethylene random copolymer (A) with the propylene-hexene random copolymer (B1), the propylene-hexene-ethylene terpolymer (B2) or a mixture thereof to obtain a mixture of (A) and (B); and
(iv) extruding said mixture to obtain the blend of (A) and (B).
8. An article comprising the polypropylene composition according to claim 1 , wherein the article comprises an unoriented film, the film having (i) a sealing initiation temperature (SIT, as calculated from DSC) of less than 114° C. and (ii) a relative total penetration energy (Wbreak) as determined by the “Dynatest” method according to ISO 7725-2 at 0° C. on a cast film with a thickness of 50 μm of more than 15.0 J/mm.
9. The article according to claim 8 , wherein the film has a sealing initiation temperature (SIT, as calculated from DSC) in the range from 105° C. to 113° C.
10. The article according to claim 8 , wherein the film has a relative total penetration energy (Wbreak) as determined by the “Dynatest” method according to ISO 7725-2 at 0° C. on a cast film with a thickness of 50 μm in the range of 16.0 to 40.0 J/mm.
11. The article according to claim 8 , wherein the film has a haze determined on 50 μm cast film of below 1.0% and a clarity determined on 50 μm cast film of above 97.0%.
12. The article according to claim 8 , wherein the article comprises an unoriented film comprising more than 90 wt % of the polypropylene composition (PP) according to claim 1 , based on the total weight of the article, wherein the film is a cast film or a blown film.