Face coating for acoustical monolithic ceilings
Described herein is a coated acoustic building material comprising a body comprising a first major surface opposite a second major surface; a coating having an upper surface opposite a lower surface, the lower surface of the coating facing the first major surface of the body, the coating comprising: polymeric binder having a glass transition temperature less than 0° C.; and a filler; wherein the coating is present as coalesced particles atop the first major surface in an amount ranging from about 210 g/m 2 to about 1,300 g/m 2 .
1. A coating composition comprising:
a polymeric binder having a glass transition temperature less than 0° C.;
a filler; and
a liquid carrier;
wherein the polymeric binder is present in an amount ranging from about 3 wt. % to about 8 wt. % based on a total weight of the coating composition.
2. The coating composition according to claim 1 , wherein the glass transition temperature of the polymeric binder is less than −20° C.
3. The coating composition according to claim 1 , wherein the polymeric binder has a minimum film formation temperature that is less than 4° C., less than or equal to about 2° C., or less than or equal to about −1° C.
4. The coating composition according to claim 1 , wherein the polymeric binder is selected from polyvinyl acetate, polyvinyl acrylic, polyurethane, polyurethane acrylic, polystyrene acrylic, epoxy, polyethylene vinyl chloride, polyvinylidene chloride, and polyvinyl chloride.
5. The coating composition according to claim 1 , wherein the coating composition has a solids content from about 65 wt. % to about 85 wt. %, based on the total weight of the coating composition.
6. The coating composition according to claim 1 , wherein the filler is selected from calcium carbonate, limestone, titanium dioxide, sand, barium sulfate, clay, mica, dolomite, silica, talc, perlite, polymers, gypsum, wollastonite, expanded-perlite, calcite, aluminum trihydrate, pigments, zinc oxide, and zinc sulfate.
7. The coating composition according to claim 6 , wherein the filler to binder ratio is at least 1:1.
8. The coating composition according to claim 7 , wherein the filler is silica.
9. A coating composition comprising:
a polymeric binder having a glass transition temperature less than 0° C. such that when the coating composition is applied to a substrate to form a coating on the substrate, the coating is present as coalesced particles;
a filler; and
a liquid carrier;
wherein the solids content of the coating composition is from about 65 wt. % to about 85 wt. % based on a total weight of the coating composition.
10. The coating composition according to claim 9 , wherein the coating composition has a viscosity ranging from about 600 cps to about 8,000 cps at 10 RPM.
11. The coating composition according to claim 9 , wherein the glass transition temperature of the polymeric binder is less than −20° C.
12. The coating composition according to claim 9 , wherein the liquid carrier is present in an amount ranging from about 21 wt. % to about 35 wt. % based on the total weight of the coating composition.
13. The coating composition according to claim 9 , wherein the polymeric binder has a film formation temperature of less than 2° C.
14. The coating composition according to claim 9 , wherein the coalesced particles have a particle size ranging from about 20 μm to about 1,000 μm.
15. A coating composition comprising:
a polymeric binder having a glass transition temperature less than 0° C. and a minimum film formation temperature less than about 10° C.;
a filler; and
a liquid carrier.
16. The coating composition according to claim 15 , wherein the polymeric binder is present in an amount ranging from about 3 wt. % to about 8 wt. % based on a total weight of the coating composition.
17. The coating composition according to claim 15 , wherein the filler comprises at least one of microfibers, powders, or pigments.
18. The coating composition according to claim 15 , wherein the filler comprises microfibers, and wherein the microfibers comprise a fibrous material having a diameter of less than about 50 μm.
19. The coating composition according to claim 15 , wherein the filler comprises silica.
20. The coating composition according to claim 15 , wherein the filler to binder ratio is at least 1:1.