Nanocomposite formulations for optical applications
The present disclosure provides a high refractive index acrylic formulation embedded with sub-10 nm metal oxide nanocrystals. The formulation is ideal for high refractive index, high transparency coating for a variety of optical applications including OLED lighting.
1. An organic light emitting diode (OLED) lighting device comprising an internal light extraction layer, wherein the internal light extraction layer comprises:
a scattering layer formed of a scattering formulation comprised of a nanocomposite binder and scatterer particles embedded in the nanocomposite binder, wherein
the nanocomposite binder comprises:
(i) a monomeric, oligomeric and/or polymeric binder material having a refractive index of between 1.60-1.90 when measured at a wavelength of 400 nm, and
(ii) high refractive index nanocrystals having an average size of less than 20 nm dispersed throughout the binder material, wherein the nanocrystals are selected from the group consisting of zirconium oxide, titanium oxide, hafnium oxide and zinc oxide, and wherein
the scatterer particles are selected from the group consisting of a polymer, titanium oxide, silicon dioxide, niobium pentoxide, zirconium oxide, zinc oxide, aluminum oxide, cerium oxide or mixtures of any two of a polymer, titanium oxide, silicon dioxide, niobium pentoxide, zirconium oxide, zinc oxide, aluminum oxide and cerium oxide; and wherein
the scatter particles are present in an amount of 0.1-40 wt. %, based on total weight of the scattering formulation, and have an average size in a range of 50 nm-500 nm, and wherein
the scattering formulation does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), and wherein
a surface roughness Ra of the scattering layer having a thickness of 1 μm is 5-4 nm, or 4-3 nm, or 3-2 nm, or 2-1 nm, or 1-0.5 nm, or 0.5-0.1 nm over an area of 1 μm by 1 μm.
2. The OLED device of claim 1 , wherein the scattering formulation is cured or partially cured.
3. The OLED device of claim 1 , wherein the nanocomposite binder has a refractive index of between 1.70-1.90 when measured at a wavelength of 400 nm.
4. The OLED device of claim 1 , wherein the scattering layer has less than 5% weight change after being treated with an acid, a base, an organic compound or water for one minute.
5. The OLED device of claim 1 , wherein the nanocrystals are present in the nanocomposite binder in an amount of 50%-93% by weight of the nanocomposite binder.
6. The OLED device of claim 1 , wherein the scattering layer is produced by spin coating, slot-die coating, slit-coating, screen-printing, ink-jet printing, dip coating, draw-bar coating, roll-to-roll printing, spray coating, or any combination thereof.
7. A display device which comprises the OLED lighting device of claim 1 .
8. A scattering film for an organic light emitting diode (OLED) lighting device, wherein the film is comprised of a scattering formulation comprising:
a nanocomposite binder and scatterer particles embedded in the nanocomposite binder; wherein
the nanocomposite binder comprises:
(i) a monomeric, oligomeric and/or polymeric binder material having a refractive index of between 1.60-1.90 when measured at a wavelength of 400 nm, and
(ii) high refractive index nanocrystals having an average size of less than 20 nm dispersed throughout the binder material, wherein the nanocrystals are selected from the group consisting of zirconium oxide, titanium oxide, hafnium oxide and zinc oxide, and wherein
the scatterer particles are selected from the group consisting of a polymer, titanium oxide, silicon dioxide, niobium pentoxide, zirconium oxide, zinc oxide, aluminum oxide, cerium oxide or mixtures of any two of a polymer, titanium oxide, silicon dioxide, niobium pentoxide, zirconium oxide, zinc oxide, aluminum oxide and cerium oxide; and wherein
the scatterer particles are present in an amount of 0.1-40 wt. %, based on total weight of the scattering formulation, and have average size in a range of 50 nm-500 nm, and wherein
the scattering formulation does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), and wherein
a surface roughness Ra of the scattering layer having a thickness of 1 μm is 5-4 nm, or 4-3 nm, or 3-2 nm, or 2-1 nm, or 1-0.5 nm, or 0.5-0.1 nm over an area of 1 μm by 1 μm.
9. The scattering film of claim 8 , wherein the scattering formulation is cured or partially cured.
10. The scattering film of claim 8 , wherein the nanocomposite binder has a refractive index of between 1.70-1.90 when measured at a wavelength of 400 nm.
11. The scattering film of claim 8 , wherein the scattering film has less than 5% weight change after being treated with an acid, a base, an organic compound or water for one minute.
12. The scattering film of claim 8 , wherein the nanocrystals are present in the scattering film in an amount of 50%-93% by weight of the nanocomposite binder.
13. The scattering film of claim 8 , wherein the film is produced by spin coating, slot-die coating, slit-coating, screen-printing, ink-jet printing, dip coating, draw-bar coating, roll-to-roll printing, spray coating, or any combination thereof.