FILM FOR GLASS LAMINATION AND METHOD FOR PREPARING SAME
The film for glass lamination of the present disclosure comprises a polyvinyl acetal resin, a plasticizer, and a metal salt, wherein the film has an adhesion control effect of 8.5 kgf/cm 2 or more per the metal salt in an amount of 10 ppm based on a total weight of the film.
1 . A film for glass lamination comprising a polyvinyl acetal resin, a plasticizer, and a metal salt, wherein the film has an adhesion control effect of 8.5 kgf/cm 2 or more per the metal salt in an amount of 10 ppm based on a total weight of the film.
2 . The film of claim 1 , wherein the film has the adhesion control effect of 8.5 to 50 kgf/cm 2 per the metal salt in an amount of 10 ppm based on the total weight of the film.
3 . The film of claim 1 , wherein the film has an uneven concentration gradient of the metal salt such that a surface of the film comprises the metal salt or metal ions derived from the metal salt in a higher concentration compared to a center of the film.
4 . The film of claim 1 , wherein the film has an adhesion control effect of 1.3 times greater compared to a reference film not having the uneven concentration gradient of the metal salt.
5 . The film of claim 3 , wherein the film contains a greater amount of the metal salt or the metal ions in both surfaces of the film compared to the center of the film.
6 . The film of claim 1 , wherein the metal salt is comprised in an amount of 200 ppm or less based on the total weight of the film.
7 . The film of claim 1 , wherein the metal ion comprised in the metal salt may be selected from the group consisting of sodium (Na) monovalent cation, magnesium (Mg) divalent cation, and potassium (K) monovalent cation.
8 . The film of claim 1 , wherein the metal salt is a benzotriazole-based compound.
9 . The film of claim 1 , wherein the film has a yellowing index variation of 2.5 or less between before and after being kept for two weeks in chamber having a constant temperature and humidity of 65° C. and 95% rh.
10 . The film of claim 1 , wherein the film has a thickness of 0.4 mm or more.
11 . A method of manufacturing a film for glass lamination comprising:
preparing a molten resin by melting a composition including a polyvinyl acetal resin, a plasticizer, and a metal salt; and
forming the film by applying a voltage to at least a part of a shaping unit for discharging and shaping the molten resin into the film,
wherein the film has an adhesion control effect of 8.5 kgf/cm 2 or more per the metal salt in an amount of 10 ppm based on a total weight of the film.
12 . The method of claim 11 , wherein the film has the adhesion control effect of 8.5 to 50 kgf/cm 2 per the metal salt in an amount of 10 ppm based on the total weight of the film.
13 . The method of claim 11 , wherein the film has an uneven concentration gradient of the metal salt such that a surface of the film comprises the metal salt or metal ions derived from the metal salt in a higher concentration compared to a center of the film.
14 . The method of claim 11 , wherein the metal salt may be comprised in an amount of 200 ppm or less based on the total weight of the film.
15 . The method of claim 11 , wherein the metal ion comprised in the metal salt may be selected from the group consisting of sodium (Na) monovalent cation, magnesium (Mg) divalent cation, and potassium (K) monovalent cation.
16 . The method of claim 11 , wherein the metal salt is a benzotriazole-based compound.
17 . The method of claim 11 , wherein the voltage applied is 8 kV or less.
18 . The method of claim 11 , wherein the shaping unit comprises an outlet, die lips in both sides of the outlet, and a voltage applying part disposed in the die lips.
19 . The method of claim 13 , wherein the voltage applied in the forming moves the metal ions comprised in the molten resin to a surface of a discharged molten resin and thereby forms the uneven concentration gradient of the metal salt.
20 . A laminate comprising the film for glass lamination of claim 1 disposed between two glasses.